Abstract:The aim of this study was to investigate the physical, mechanical, morphological, structural, and thermal properties of polylactic acid (PLA) and polyhydroxybutyrate (PHB) biopolymer composites reinforced with thermally treated wood flour and to determine the formulations having optimum properties by using multi-criteria decision-making (MCDM) methods. As a filler, Scots pine wood flour (untreated and thermally treated at 212 °C) was used at the loading rates of 10% and 30%. The samples were prepared using a twin-screw extruder and then by compression molding. The results showed that the addition of both thermally treated and untreated wood flour slightly increased the density of the composites. According to the color measurement, the thermally treated wood composites were slightly darkened in appearance. In the composites, with both wood fillers, the water absorption and thickness swelling ratios had increased during the 20–250 days of water exposure. Lower water absorption and thickness swelling rates were found for the composites with thermally treated wood filler compared to the other composites. The wood fillers generally lowered the mechanical properties of the PLA and PLA/PHB composites, with the PHB composites as the exception. However, the tensile modulus and Izod impact strength of the composites generally increased with the addition of wood fillers. Morphological examination performed by scanning electron microscopy (SEM) indicated that the wood flour was mostly homogeneously distributed in the matrix, which improved the mechanical properties of the composites. Thermogravimetric analysis (TGA) showed that the addition of wood filler to the neat biopolymers as a rule did not provide significant improvement in the thermal stability; however, the fillers increased the thermal stability of neat PHB. The Fourier-transform infrared (FTIR) spectroscopy detected no differences in the chemical structure of the composites. The X-ray diffraction (XRD) results indicated a general increase in the crystallinity with the addition of wood fillers to the neat biopolymers and the blends. All the findings were subjected to MCDM analysis to determine the formulation having the optimum properties and the results showed this to be the neat PLA sample.

Preparation, characterization, and performance of bio-based polyester composites derived from renewable distillers grains and shellfish

Toughness Enhancement of Poly(lactic Acid), Bamboo Particle and Ultrafine Bamboo-Char Ternary Biocomposites by Polyethylene Glycol Plasticization

Wood Flour-Reinforced Green Composites: Parameter Optimization via Multi-criteria Decision-Making Methods

Preparation and Characterization of Polylactic Acid/Bamboo Fiber Composites.

High-performance polylactic acid composites reinforced by artificially cultured diatom frustules

Influence of carboxy-terminated hyperbranched polyester and polyethylene glycol on the mechanical and thermal properties of polylactic acid/straw flour composites

PLA-Based Biodegradable Copolyester Nanocomposites: Preparation, Characterization and Mechanical Properties

Toughening and Heat-Resistant Modification of Degradable PLA/PBS-Based Composites by Using Glass Fiber/Silicon Dioxide Hybrid Fillers

Thermo-Blending of Biobased Poly(propylene 2,5-furan dicarboxylate) and Poly(lactic acid) with Improved Mechanical Performance

Barrier Properties and Hydrophobicity of Biodegradable Poly(lactic acid) Composites Reinforced with Recycled Chinese Spirits Distiller’s Grains

Effects of Chitosan Nanoparticles and 4,4′ Methylene-Diphenyl Diisocyanate on the Polylactic Acid/Poly (Butyleneadipate-Co-Terephthalate) Composite Properties

Fabrication and characterization of poly(lactic acid-trimethylene carbonate) based biodegradable composite films

Super‐ductile and Stiff PBAT/PLA Biodegradable Composites Balanced with Random PMMA‐co‐GMA Copolymer As Compatibilizer

Construction of high-performance and sustainable polylactic acid composites for 3D printing applications with plasticizer

Bio-based Green Composites with High Performance from Poly(lactic Acid) and Surface-Modified Microcrystalline Cellulose

Preparation and characterization of bio-based green renewable composites from poly(lactic acid) reinforced with corn stover

Preparation and properties of PLA/PBAT composites modified with different filler particles

Development of PLA/Lignin Bio-Composites Compatibilized by Ethylene Glycol Diglycidyl Ether and Poly (ethylene glycol) Diglycidyl Ether

Synergistic modification of polylactic acid by oxidized straw fibers and degradable elastomers: A green composite with good strength and toughness

Study on modified poplar wood powder/polylactic acid high toughness green 3D printing composites

Poly(l-lactide)/poly(d-lactide)/bamboo fiber (BF) bio-composites with enhanced heat resistance, mechanical and rheological performance