Abstract:Two ingots weighing 400 g and 5 kg with nominal compositions of Fe-8Mn-4Al-2Si-0.5C-0.07V-0.05Sn were produced to investigate the effect of processing variables on microstructure development. The larger casting has a cooling rate more representative of commercial production and provides an understanding of the potential challenges arising from casting-related segregation during efforts to scale up medium Mn steels, whilst the smaller casting has a high cooling rate and different segregation pattern. Sections from both ingots were homogenised at 1250 \degree C for various times to study the degree of chemical homogeneity and $\delta$-ferrite dissolution. Within 2 h, the Mn segregation range (max $-$ min) decreased from 8.0 to 1.7 wt\% in the 400 g ingot and from 6.2 to 1.5 wt\% in the 5 kg ingot. Some $\delta$-ferrite also remained untransformed after 2 h in both ingots but with the 5 kg ingot showing nearly three times more than the 400 g ingot. Micress modelling was carried out and good agreement was seen between predicted and measured segregation levels and distribution. After thermomechanical processing, it was found that the coarse untransformed $\delta$-ferrite in the 5 kg ingot turned into coarse $\delta$-ferrite stringers in the finished product, resulting in a slight decrease in yield strength. Nevertheless, rolled strips from both ingots showed $>$900 MPa yield strength, $>$1100 MPa tensile strength and $>$40\% elongation with $<$10\% difference in strength and no change in ductility when compared to a fully homogenised sample.

Significance of segregation on grain refinement and property improvement in extruded Mg-Al-Mn alloy with moderate Al content

Microstructure Evolution and Properties of Mg-9Gd-0.8Al Alloy with Lamellar Phase During Extrusion at Different Temperatures

Effect of Mo on Segregation Behavior of Al-Mg-Si-Mn Alloy Produced by Twin-Roll Casting

A scale up study on chemical segregation and the effects on tensile properties in two medium Mn steel castings

Effect of Grain Size on Tensile Deformation Behavior of Nano-Polycrystalline Al and Al–Mg Alloys with Grain Boundary Segregation of Mg

Understanding the Extrusion Microstructures in Mg Alloys Due to Solute Segregation

Recrystallization and Microstructural Evolution During Hot Extrusion of Mg 97 Y 2 Zn 1 Alloy

Effect of extrusion parameters on microstructure and mechanical properties of Mg-0.12Ca-0.08Ba alloy

Effect of High Mn Content on Development of Ultra-Fine Grain Extruded Magnesium Alloy

Microstructural Evolution and Mechanical Properties of Mg-5y-5gd-Xnd-0.5zr Magnesium Alloys at Different States

Evolution of Microstructures, Texture, Damping and Mechanical Properties of Hot Extruded Mg-Nd-Zn-Zr Alloy

Evolution of Microstructure and Tensile Properties of Extruded Mg-4Zn-1Y Alloy

Enhancing mechanical properties of twin-roll cast Al–Mg–Si–Fe alloys by regulating Fe-bearing phases and macro-segregation

Microstructures and Mechanical Properties of Hot-extruded Mg-6Zn-xCu-0.6Zr(x=0,0.5,1.0,1.5) Alloys

Microstructure and mechanical properties of Mg-Gd-Zn-Zr alloy after hot extrusion

Unraveling the Enhanced Stability and Strength of Al Σ9 (221)[$$ 1\bar{1}0 $$] Symmetric Tilt Grain Boundary with Mg Segregation

Grain Coarsening Behavior of Mg-Al Alloys with Mischmetal Addition

First-principles investigation of the Mg, Cu segregation at Al Σ5 (310) and Σ9 (221) symmetrical tilt grain boundaries

Mechanical Properties and Microstructures of Mg-Al-Zn Alloys with High Aluminum Contents

Influence of Mg17Al12 Intermetallic Compounds on the Hot Extruded Microstructures and Mechanical Properties of Mg–9Al–1Zn Alloy

The Effects of Grain Refinement and Rare Earth Intermetallics on Mechanical Properties of As-Cast and Wrought Magnesium Alloys