The effect of gradient order on impact toughness of carbon S38C steels with induction hardening

Han Zhang,Shengchuan Wu,Ni Ao,Liang Zhou,Lianqing Wang,Dong Liu

DOI: https://doi.org/10.1016/j.engfailanal.2023.107254

IF: 4

2023-04-17

Engineering Failure Analysis

Abstract:Induction hardened S38C axles exhibit the balance between good crack growth resistance at the body and wear resistance at the wheel seat, which can be attributed to the gradient structure with fine grains (FG) near the surface and coarse grains inside the base metal (BM). However, the impact toughness of such bulk gradient structure is less reported when experiencing high-speed impacts. Therefore, the impact behaviors of the S38C steel are thoroughly examined by using the V-notch instrumented Charpy impact testing. It is clearly found that the gradient order has a significant effect on the impact response. For the gradient structure termed as FG→BM, the absorbed energy is significantly lower than the BM structure but the higher strength and hardness, which indicates that the FG→BM structure is difficult to tailor the fatigue crack growth and the resulting fatigue life of railway axles. By contrast, the BM→FG structure exhibits more excellent impact resistance primarily owing to the micropore coalescence. To acquire the exceptional damage tolerance, the inner bore and external surface of the S38C axles can be sequentially strengthened to acquire an integrated gradient structure.

engineering, mechanical,materials science, characterization & testing