Effect of Vanadium Content on the Microstructure and Mechanical Properties of IN718 Alloy by Laser Cladding

Hao Lv,Zhijie Li,Xudong Li,Kun Yang,Fei Li,Hualong Xie

DOI: https://doi.org/10.3390/ma14092362

IF: 3.4

2021-05-01

Materials

Abstract:Microalloying vanadium can change the segregation state of Nb element in IN718 alloy, reduce the formation of harmful Laves phase and refine the dendritic structure of IN718 alloy during the laser process. Therefore, IN718 alloys with V content from 0.081 to 1.88 wt.% were prepared and evaluated. Metallographic microscopy and scanning electron microscopy were used to observe the corresponding morphology, structure, and distribution of elements. First of all, it was found that the addition of V refines the grain size of IN718 alloy and reduces the primary dendrite arm spacing. Secondly, adding V to IN718 alloy can reduce the porosity of the cladding layer. The elements are uniformly distributed in the cladding layer, and the addition of vanadium reduces the segregation degree of the Nb element, which is conducive to homogenization. In addition, microhardness and residual stress were also investigated. Finally, the addition of vanadium was shown to have no apparent effect on the tensile strength and yield strength but can significantly improve the elongation of IN718 alloy. In conclusion, the microstructure and mechanical properties of IN718 alloy with 0.081 wt.% vanadium content provide a new solution to improve the application level of IN718 alloy in laser cladding.

materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

The paper mainly explores the effects of different vanadium (V) contents on the microstructure and mechanical properties of IN718 alloy during the laser cladding process.

### Problems the Paper Attempts to Solve

1. **Improvement of Laves Phase Issue**: IN718 alloy experiences severe compositional segregation during the solid-state process, leading to the formation of harmful Laves phases, which degrade the material's performance. The paper attempts to alter the segregation state of niobium (Nb) by adding different amounts of vanadium to reduce the formation of harmful Laves phases and refine the dendritic structure of the IN718 alloy.

2. **Optimization of Microstructure and Enhancement of Mechanical Properties**: By controlling the extent of the Laves phase, the paper aims to improve the microstructural characteristics of the IN718 alloy, thereby affecting its mechanical properties. Different amounts of vanadium (ranging from 0.081 wt.% to 1.88 wt.%) were added in the study to find the optimal vanadium content to enhance the overall performance of the IN718 alloy.

3. **Evaluation of Vanadium's Impact on Porosity, Hardness, and Residual Stress**: In addition to microstructure and mechanical properties, the paper also investigates the changes in porosity, microhardness, and residual stress of the alloy after adding vanadium.

### Main Findings

- Adding vanadium can refine the grain size of the IN718 alloy and reduce the primary dendrite arm spacing.
- Adding vanadium can decrease the porosity of the cladding layer and make the element distribution more uniform.
- Microhardness and residual stress are also affected by the addition of vanadium.
- Although the addition of vanadium does not significantly impact tensile strength and yield strength, it can significantly improve the elongation of the IN718 alloy.

In summary, the paper aims to improve the microstructure and mechanical properties of the IN718 alloy by adding an appropriate amount of vanadium, particularly optimizing the Laves phase issue, thereby enhancing the application level of this alloy in the laser cladding process.