Steam Reactivation of Biotemplated CaO-Based Pellets for Cyclic CO 2 Capture

Nai Rong,Yan Wu,Jiuheng Wang,Long Han,Geng Wang

DOI: https://doi.org/10.1021/acs.energyfuels.1c00361

2021-03-16

Abstract:The calcium-based sorbents with a starch pore former and a cement stabilizer were fabricated via the extrusion–spheronization approach for high-temperature CO₂ capture. The addition of a 10% starch template and 20% cement in the sorbent led to the highest CO₂ uptake of 0.15 g/g after 20 cycles. With increasing cycle numbers, the gradual decline in CO₂-capture capacity was still observed for the modified sorbents. To restore the CO₂-capture performance, steam reactivation with various frequencies, steam concentrations, and operational strategies was adopted. After 20 cycles, the CO₂ uptake stabilized at around 0.41 g/g for the modified sorbent with separate steam hydration after every calcination. The steam introduction during carbonation or calcination recovered the CO₂ uptake to 0.27 g/g after 20 cycles, which was almost 2 times higher than that of the pellets cycled without steam introduction. Steam hydration reactivation exhibited negative impacts on the mechanical strength of the templated sorbent. The pellets collected after tests with hydration after every 1/3/5 cycles displayed breaking forces less than 1 N, in comparison to the value of 8.82 N for the pellets without hydration. The inferior mechanical strength was attributed to the volume expansion/contraction of pellets during the hydration–dehydration procedure.This article has not yet been cited by other publications.

energy & fuels,engineering, chemical