Abstract:This study aimed to evaluate in vitro the effect protocols and anticaries agents containing casein amorphous calcium fluoride phosphopeptide-phosphate (CPP-ACPF, MI Paste Plus), sodium trimetaphosphate (TMP) and fluoride (F), in remineralization of caries lesions. Bovine enamel blocks with initial caries lesions were divided into groups (n = 12): 1) Toothpaste without F-TMP-MI Plus (Placebo); 2) Toothpaste 1100 ppm F (1100F), 3) 1100F + MI Paste Plus (1100F-MI Paste Plus), 4) Toothpaste with 1100F + Neutral gel with 4,500 ppm F + 5%TMP (1100F + Gel TMP) and 5) Toothpaste with 1100F + Neutral gel with 9,000 ppm F (1100F + Gel F). For the 4 and 5 groups the gel was applied only once for 1 minute, initially to the study. For the 3 group, after treatment with 1100F, MI Paste Plus was applied 2x/day for 3 minute. After pH cycling, the percentage of surface hardness recovery (%SHR); integrated loss of subsurface hardness (ΔKHN); profile and depth of the subsuperficial lesion (PLM); concentrations of F, calcium (Ca) and phosphorus (P) in enamel was determined. The data were analyzed by ANOVA (1-criterion) and Student-Newman-Keuls test (p < 0.001). Treatment with 1100F alone led to ~ 28% higher remineralization when compared to treatment with 1100F associated with MI Paste Plus (p < 0.001). The 1100F and 1100F + Gel F groups showed similar values for %SHR (p = 0.150). 1100F + Gel TMP treatment also remineralized the enamel surface by ~ 30% and 20% when compared to the 1100F + Gel F and 1100F groups (p < 0.001). The lower lesion depth (ΔKHN) was observed for the 1100F + Gel TMP group (p < 0.001), where it was 54% and 44% lower in comparison to the 1100F and 1100F + Gel F groups (p < 0.001). Polarized light microscopy photomicrographs showed subsurface lesions in all groups, but these lesions were present to a lower extent in the 1100F + Gel TMP group (p < 0.001). Treatment with 1100F + Gel TMP promoted an increase in the concentration of Ca in the enamel by ~ 57% and ~ 26% when compared to the 1100F and 1100F + MI Paste Plus groups (p < 0.001), respectively. There were no significant differences between the 1100F, 1100F + MI Paste Plus and 1100F + Gel F groups (p > 0.001). Similar values of P in the enamel were observed in the 1100F, 1100F + MI Paste Plus and 1100F + Gel F groups (p > 0.001), except for the 1100F + Gel TMP group, which presented a high concentration (p < 0.001). We conclude that the 1100F+TMP gel treatment/protocol led to a significant increased remineralization when compared to the other treatments/protocols and may be a promising strategy for patients with early caries lesions.

Biomineralization and remineralizing potential of toothpastes containing nanosized β-calcium glycerophosphate: an in vitro study

Effect of treatment with phosphate, casein phosphopeptide and fluoride on the remineralization: in vitro study

Antibacterial and Remineralization Efficacy of Casein Phosphopeptide, Glycomacropeptide Nanocomplex, and Probiotics in Experimental Toothpastes: An In Vitro Comparative Study

Effects of Different Toothpastes on the Nanomechanical Properties and Chemical Composition of Resin-Modified Glass Ionomer Cement and Composite Resin Restorations

Dental tissue remineralization by bioactive calcium phosphate nanoparticles formulations

An in vitro study of remineralization potential of several toothpastes on initial enamel lesions

Effect of the β-tricalcium phosphate particle on dental enamel associated with 10% carbamide peroxide bleaching

Remineralization Efficacy of A Toothpaste Containing 8% Arginine and Calcium Carbonate on Enamel Surface

Caries-preventive effect of anti-erosive and nano-hydroxyapatite-containing toothpastes in vitro

Enamel Remineralization and Dentine Tubules Occlusion by Bioactive Formulations Based on Ion-Doped Nanohydroxyapatite and Precursor Nanoparticles.

In Vitro Evaluation of Remineralization Potential of Five Toothpastes on Soft Drink-Eroded Human Enamel and Dentine

Inorganic Phosphate Effect in a Hydrogen Peroxide-based Bleaching Agent: Physicochemical, Mechanical, and Morphological Properties of Dental Enamel

In situ remineralization of white-spot enamel lesions by 500 and 1,100 ppm F dentifrices

Enhanced Anti-Biofilm and Anti-Caries Potential of Arginine Combined with Calcium Glycerophosphate and Fluoride

Effects of different toothpastes on the prevention of erosion in composite resin and glass ionomer cement enamel and dentin restorations

Fluoride-amorphous calcium phosphate and biomimetic nano-hydroxyapatite for enamel remineralization: An in-vitro study of surface microhardness and composition

Remineralization Effectiveness of Adhesive Containing Amorphous Calcium Phosphate Nanoparticles on Artificial Initial Enamel Caries in a Biofilm-Challenged Environment

In situ efficacy of an experimental toothpaste on enamel rehardening and prevention of demineralisation: a randomised, controlled trial

Effect of calcium phosphate nanocomposite on in vitro remineralization of human dentin lesions.

The Remineralization Effect of Calcium Glycerophosphate in Fluoride Mouth Rinse on Demineralized Primary Enamel: An in vitro Study

SEM/EDS Evaluation of the Mineral Deposition on a Polymeric Composite Resin of a Toothpaste Containing Biomimetic Zn-Carbonate Hydroxyapatite (microRepair®) in Oral Environment: A Randomized Clinical Trial