Rare-earth ions induced pre-excitation of intercalation-conversion anode to achieve fast potassium-ion storage

Yongpeng Cui,Lina Ge,Wenting Feng,Li Zhou,Pengyun Liu,Xuejin Li,Debin Kong,Qingzhong Xue,Eslam Sheha,Yongfu Tang,Wei Xing

DOI: https://doi.org/10.1016/j.ensm.2024.103425

IF: 20.4

2024-04-25

Energy Storage Materials

Abstract:K-ions storage system play an important role in the up-coming clean-energy era. However, its performance is severely restricted by the difficulties in the insertion and diffusion of large-sized K-ions. In this work, a rare-earth ion induced pre-excitation strategy is proposed to significantly improve the K-ion storage performance of MoSe 2 -based anode materials. A series of rare-earth ions (Re = Lu 3+ , Tm 3+ , Y 3+ , Gd 3+ , Sm 3+ , Nd 3+ , and La 3+ ) are introduced into the Se-Mo-Se basal plane (labeled as Re-MoSe 2-x @C), resulting in the abundance of fracture surfaces with active sites (Se-vacancy) up to 14.2% and increased interlayer spacing. Interestingly, such structure with sufficient active Se-vacancy defects enable K-ions to be preferentially adsorbed onto the fractured Se-Mo-Se basal plane. Subsequently, these adsorbed K-ions cross the layered plane through the defect sites, rather than the edge sides, to complete the subsequent facilitated intercalation and conversion reaction. Thanks to this well-integrated mechanism, the assembled K-ion capacitor delivers an outstanding energy/power characteristic (form 146 Wh kg −1 /500 W kg −1 to 86 Wh kg −1 /10 kW kg −1 ) and cycling stability (nearly 100% retention after 10000 cycles), demonstrating its promising prospects in practical applications.

materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology