Initial Characteristics of Alkali–Silica Reaction Products in Mortar Containing Low-Purity Calcined Clay

Daria Jóźwiak-Niedźwiedzka,Roman Jaskulski,Kinga Dziedzic,Aneta Brachaczek,Dariusz M. Jarząbek
DOI: https://doi.org/10.3390/ma17102207
IF: 3.4
2024-05-09
Materials
Abstract:An alkali–silica reaction (ASR) is a chemical process that leads to the formation of an expansive gel, potentially causing durability issues in concrete structures. This article investigates the properties and behaviour of ASR products in mortar with the addition of low-purity calcined clay as an additional material. This study includes an evaluation of the expansion and microstructural characteristics of the mortar, as well as an analysis of the formation and behaviour of ASR products with different contents of calcined clay. Expansion tests of the mortar beam specimens were conducted according to ASTM C1567, and a detailed microscopic analysis of the reaction products was performed. Additionally, their mechanical properties were determined using nanoindentation. This study reveals that with an increasing calcined clay content, the amount of the crystalline form of the ASR gel decreases, while the nanohardness increases. The Young's modulus of the amorphous ASR products ranged from 5 to 12 GPa, while the nanohardness ranged from 0.41 to 0.67 GPa. The obtained results contribute to a better understanding of how the incorporation of low-purity calcined clay influences the ASR in mortar, providing valuable insights into developing sustainable and durable building materials for the construction industry.
materials science, multidisciplinary,metallurgy & metallurgical engineering,physics, applied,chemistry, physical, condensed matter
What problem does this paper attempt to address?
The paper attempts to address the durability issues caused by Alkali-Silica Reaction (ASR) in concrete structures. Specifically, the study aims to investigate the effects of adding low-purity calcined clay to mortar on the characteristics and behavior of ASR products. By evaluating the expansion and microstructural characteristics of the mortar, and analyzing the impact of different contents of calcined clay on the formation and behavior of ASR products, the research hopes to provide insights into how low-purity calcined clay affects ASR in mortar, thereby offering valuable references for developing sustainable and durable building materials. ### Main Research Content: 1. **Background Introduction**: - Alkali-Silica Reaction (ASR) is a chemical process that leads to the formation of expansive gel in concrete, causing structural cracking and durability issues. - ASR is a multi-stage process that requires three conditions: a high alkaline environment, the presence of reactive silica, and a moist environment. - Traditional methods to inhibit ASR include using aggregates that do not contain reactive silica or reducing the alkali content, but these methods can limit the use of certain raw materials. 2. **Research Objectives**: - To evaluate the effects of low-purity calcined clay on the physical, chemical, and microstructural characteristics of ASR products in mortar. - Through experiments and analysis, to understand how low-purity calcined clay affects the long-term performance and durability of mortar. 3. **Experimental Methods**: - Using the ASTM C1567 standard method to test the expansion degree of mortar samples. - Preparing mortar samples with different proportions of calcined clay and conducting microstructural analysis. - Using Scanning Electron Microscopy (SEM) and Energy Dispersive X-ray Spectroscopy (EDX) to analyze the morphology and chemical composition of ASR products. - Evaluating the mechanical properties of ASR products using nanoindentation techniques. 4. **Results and Discussion**: - With the increase in calcined clay content, the crystalline form of ASR gel decreases, and nano-hardness increases. - The Young's modulus of ASR products ranges from 5 to 12 GPa, and the nano-hardness ranges from 0.41 to 0.67 GPa. - Mortar samples containing 20% and 30% calcined clay have an expansion rate of less than 0.1% within 14 days, while the reference mortar and mortar samples containing 10% calcined clay exceed the 0.1% expansion limit within 14 days. - Microstructural analysis shows that with the increase in calcined clay content, the morphology and chemical composition of ASR products change, especially in the cement matrix, where the Ca/Si and alkali/Si ratios decrease. ### Conclusion: The study reveals the significant impact of low-purity calcined clay on ASR products in mortar, providing important scientific evidence for the development of sustainable and durable building materials. By rationally utilizing low-purity calcined clay, ASR can be effectively inhibited, improving the durability and stability of concrete structures.