Abstract:A hydrothermal procedure was utilized to synthesize high silica H-ZSM-5 catalysts for application in methanol to olefin (MTO) reaction by partial and total substitution of tetrapropyl ammonium hydroxide (TPAOH) with equivalent amount of the less expensive tetrapropyl ammonium bromide (TPABr) template. Five H-ZSM-5 zeolites with a similar Si/Al ratio (200) were synthesized using various proportions of TPAOH and TPABr. The TPA+ concentration (0.04 M) and initial gel pH (10.5) were constant. The catalysts were characterized by TG–DTA, XRD, ICP, FE-SEM, BET, FT-IR and NH3-TPD techniques. The samples showed cubic morphology, but their particle sizes and shapes were different. The highest crystallinity were obtained by single template synthesis for MFI structure whereas using mixed template synthesis led to lower crystallinity and larger crystallite sizes. Increasing molar ratio of TPAOH in initial gel from 0.33 to 3 decreased the purity of H-ZSM-5, and also affected its crystallinity and particle size. The NH3-TPD results indicated that both TPAOH and TPABr templates exhibited almost the same effect on the acidity of the as-synthesized catalysts, whereas mixing the two templates increased the total acidity and decreased the content of strong acid site. The catalytic performance of all samples was evaluated in MTO reaction in a fixed-bed reactor at 480 °C and atmospheric pressure using feed containing a mixture of 50 wt% methanol in water with methanol WHSV of 0.9 h−1. All the catalysts exhibited approximately similar methanol conversion though their propylene selectivities and products distributions were greatly dependent on the template composition. This work verified that despite providing the same TPA+ and OH− concentrations in the initial gel, the H-ZSM5 samples with different properties could form using diverse template combinations.

Synthesis of hierarchical ZSM‐5 using polymer macro template for selective C‐alkylation of m‐cresol with tert‐butanol

EFFECT OF LONG CHAIN CATIONIC SURFACTANT ON ZSM-5 SYNTHESIS AND METHANOL TO OLEFIN REACTION

Synthesis of Hierarchical Micro-mesoporous ZSM-5 Zeolite and its Catalytic Activity in Benzylation of Mesitylene

Preparation of 2-t-Butyl-p-cresol Catalyzed by Hβ Zeolite

ZSM-5 Catalysts for MTO: Effect and Optimization of the Tetrapropylammonium Hydroxide Concentration on Synthesis and Performance.

Hydrothermal synthesis of H-ZSM-5 catalysts employing the mixed template method and their application in the conversion of methanol to light olefins

Tuning Hierarchical ZSM-5 Zeolite for Both Gas- and Liquid-Phase Biorefining

Alkylation of Phenol with Methanol over ZSM‐5 Zeolite

Catalytic Performance of Methanol to Aromatics over Hierarchical ZSM-5 Zeolite Synthesized by a Soft Template Method

Enhancing propene selectivity in methanol and/or butene conversion by regulating channel systems over ZSM-5/ZSM-48 composite zeolites

Hierarchical ZSM-5 catalytic performance evaluated in the selective oxidation of styrene to benzaldehyde using TBHP

Catalytic oxidation of isoamyl alcohol on modified ZSM-5 molecular sieve catalysts prepared by different methods

Renewable Butene Production through Dehydration Reactions over Nano-HZSM-5/γ-Al2O3 Hybrid Catalysts

Facile synthesis of hierarchical macro/microporous ZSM-5 zeolite with high catalytic stability in methanol to olefins

A novel anionic surfactant as template for the development of hierarchical ZSM-5 zeolite and its catalytic performance

Synthesis of hierarchical ZSM-11 and its catalytic performances during methanol to propylene

High-efficient hierarchical [B]-ZSM-5 catalyst by simultaneously using of CTAB surfactant and boron promoter for methanol to olefins reaction

Controllable Synthesis of Nano-Zsm-5 Catalysts with Large Amount and High Strength of Acid Sites for Conversion of Methanol to Hydrocarbons

Palladium-doped hierarchical ZSM-5 for catalytic selective oxidation of allylic and benzylic alcohols

An Efficient and Mild Method for the Alkylation of p-Cresol with tert-Butyl Alcohol

Hierarchical Zsm-5 Catalyst Synthesized by A Triton X-100 Assisted Hydrothermal Method