Synthesis and characterizations of upconverting luminescent Er 3+ / Yb 3+ : Gd 2 O 3 uniform nanospheres for biomedical applications

Tran Kim Anh,Vu Thi Thai Ha,Nguyen Thanh Huong,Do Thi Thao,Tien Dai Nguyen,Dang Van Thai,Robert Tomala,Le Quoc Minh
DOI: https://doi.org/10.1088/1402-4896/ad7c03
2024-09-19
Physica Scripta
Abstract:We present the synthesis of Er 3+ / Yb 3+ co-doped Gd 2 O 3 nanospheres using the wet-chemical method followed by a synergistic step-by-step calcination process, a novel approach in the field. The nanospheres exhibited red color upconversion luminescence (UCL) after multi-step annealing at temperatures ranging from 650 °C to 1150 °C, achieving a fully spherical morphology. The diameter and surface morphology of the nanospheres were significantly altered by the annealing process, decreasing from 382.77 ± 1.72 nm with a smooth surface to 245.7 ± 1.31 nm with a rougher surface. The UCL intensity increased with the annealing temperature. The influence of Er 3+ / Yb 3+ co-doped Gd 2 O 3 nanospheres, excited by a 975 nm laser, was investigated, and the decay time for UCL samples was analyzed. The luminescence peak at 1026 nm was attributed to the 4 I 11/2 (Er 3+ ) + 2 F 7/2 (Yb 3+ ) → 4 I 15/2 (Er 3+ ) + 2 F 5/2 (Yb 3+ ) transition/ or 2 F 5/2 → 2 F 7/2 of the Yb 3+ ions within the Gd 2 O 3 matrix. Furthermore, the UCL properties of Er 3+ / Yb 3+ co-doped Gd 2 O 3 nanophosphors were explored to detect the NTERA-2 cancer cells. These findings suggest that the rare earth co-doped Gd 2 O 3 nanospheres might hold significant potential for biomedicine and imaging diagnostics applications, sparking new interest and possibilities in these fields.
physics, multidisciplinary
What problem does this paper attempt to address?