Abstract:Epoxy resin carbons are of high strength, high temperature resistance, and corrosion resistance, which are widely used as the precursor of carbon composite materials. However, the applications of epoxy resin carbons are greatly limited for the characteristic of non-graphitization and low char yield (22 wt%). In this paper, coal tar pitch was used to modify epoxy resin carbons via a simple heating mixing, pyrolysis and high temperature graphitization. The results show that the coal tar pitch content and heat treatment temperature can improve the ordered graphite carbon content. As the coal tar pitch content increase, the ordered graphite carbon content of modified epoxy resin carbon increase after 3000 °C graphitization for 0.5 h. Particularly, the graphitization degree of epoxy resin carbon and 40 wt% coal tar pitch modified epoxy resin carbon are 8.42 % and 44.21 %, respectively. The grain size (L c = 13.84 nm) and grain stacking height (L a = 7.79 nm) of 40 wt% coal tar pitch modified epoxy resin carbon are bigger than epoxy resin carbon (L c = 3.44 nm, L a = 3.45 nm). The ordered coal tar pitch graphite carbon and disordered epoxy resin amorphous carbon are evenly distributed in the modified epoxy resin carbon, indicating a good comparability of coal tar pitch and epoxy resin. Besides, the entangling carbon ribbon are observed in the epoxy resin carbon after graphitization at 3000 °C. With the increase of coal tar pitch content, the content of carbon element, aromatic ring number, the char yield and thermal decomposition temperature of modified epoxy resin increased. Moreover, the char yield of expoxy resion modified by 50 wt% coal tar pitch is 42 wt%, almost two times higher than that of epoxy resin (22 wt%). The increased char yield of modified epoxy resin mainly inherited the high char yield of coal tar pitch (50 wt%) and the chemical crosslinking weight gain. More interesting, the chemical crosslinking weight gain reaches the maximum value of 15 wt% when the content of coal tar pitch is 40wt%. The reason for that is the possible chemical crosslinking reaction can be occured by the epoxy group and hydroxyl group within epoxy resin and carboxyl group and phenolic hydroxyl group within coal tar pitch. This study provides some theory foundation for the future application of epoxy resin carbon composite materials.

Preparation of high-performance binderless carbon material with coal-tar pitch as raw material

Preparation of micro-porous monolithic activated carbon from anthracite coal using coal tar pitch as binder

Pyrolysis mechanism of composite binder composed of coal tar pitch and phenolic resin for carbon materials

The Effect of Oxygen Content in Binderless Cokes for High-Density Carbon Blocks from Coal Tar Pitch

Effect of binder composition on the preparation of formed coke with low-rank coal

Preparation and characterization of pitch coke from oxidized polymerized pitch

Preparation of formed coke product as a coke substitute using a solid waste fuel: Trimethylbenzene improvement on coal tar pitch

Preparation and Characterization of Mesocarbon Microbeads by the Co-Polycondensation of High-Temperature Coal Tar Pitch and Coal Pyrolytic Extracts

Binding Natural Graphite with Mesophase Pitch: A Promising Route to Future Carbon Blocks

Effect of coal tar pitch modification on the structure and char yield of pyrolysis epoxy resin carbons

Response surface optimization of pitch phase change densification using composite phenolic resin co-carbonization to prepare high performance carbon refractories

Enhancement of coal tar pitch carbonization with biochar: A metallurgical formed biocoke product produced by waste coke breeze and bamboo powder

Preparation of mesocarbon microbeads from coal tar pitch with blending of biomass tar pitch

Microstructure and mechanical properties of pitch based mixture modified by additions of graphene oxide precursor and TiB2 particles

In-Situ Doping B4C Nanoparticles in Mesophase Pitch for Preparing Carbon Fibers with High Thermal Conductivity by Boron Catalytic Graphitization

Preparation of Mesophase Pitch with Fine-Flow Texture from Ethylene Tar/Naphthalene by Catalytic Synthesis for High-Thermal-Conductivity Carbon Fibers

Puffing behavior during the carbonization of lignin-collagen based green composites

Preparation and Performance of Mesophase Pitch Based Graphite Foam

Gas Phase‐Heat Absorption‐Condensate Phase Stepwise Flame Retardant Strategy to Prepare Coal Tar Pitch‐Based Porous Carbon for Supercapacitor

Mesophase formation of coal-tar pitches used for impregnant of C/C composites

Effects of Oxygen Content of Pitch Precursors on the Porous Texture and Surface Chemistry of Pitch-Based Activated Carbon Fibers