Puffing behavior during the carbonization of lignin-collagen based green composites

Zilong ZHAO,Hongjie WANG,Wenyi DONG

DOI: https://doi.org/10.11918/j.issn.0367-6234.201608016

2018-01-01

Abstract:Biomass solid wastes, such as lignin and collagen, are potentialized to be developed as coal tar pitch alternatives to prepare the carbon products. However, controlling the puffing behavior during the carbonization is a key factor to obtain the excellent carbon materials. In the present study, green composites using the pine softwood lignin and collagen as hybrid binder were prepared by the hot-pressing process. The effect of baking program and puffing inhibitors on the puffing behavior was evaluated. Elemental analysis and Scanning Electronic Microscopy ( SEM) were also employed for further study. Results showed that a lower heating rate ( baking rate of 0.04℃/min to 500℃, then 0.07 ℃/min to 500-800 ℃) and a higher cooling rate (1.08 ℃/min) were preferred for puffing inhibition. Some traditional puffing inhibitors, such as coconut shell, lignite coal feed, boric acid, ferric oxide, and iron (Ⅲ) chloride, were not available to the bio-binder system. Along with the improvement of puffing inhibition, the apparent density of the baked product gradually decreased. In the case of a mixture system containing ferric oxide, the rising temperature promoted the enrichment of carbon element and the decrease of other elements such as N, S, and O, resulting in fluctuating change in Fe content. The lignin/collagen hybrid system served as thermally-fused binder to form a new integrated char with turbostratic structure by means of covering, filling and bridging, and iron precipitates derived from ferric oxide was observed on the surface of char during the graphitization.