Abstract:Nickel-based single crystal superalloys, as engine blade materials, are prone to fatigue damage due to repeated startups and shutdowns. Therefore, monitoring and quantitatively estimating fatigue cracks are essential for engineering structures to ensure safety. In this study, we proposed a method for fatigue crack segmentation and damage prediction based on deep learning and in-situ high-temperature scanning electron microscopy (SEM). Sequential SEM images describing the crack initiation and propagation under near-service conditions were obtained by conducting in-situ high-temperature fatigue experiments. A fatigue crack dataset with high-quality was thus constructed for further dynamic and real-time crack segmentation and damage assessment. Deep learning-based models were used to segment cracks and predict damage behavior (i.e., crack area, length, width, and stress intensity factors) at future based on prior damage information. The short-term and long-term damage prediction capability were validated by comparing model performance when predicting damage at different future time points. Additionally, we compared the model performance when predicting damage at specific time point based on varying lengths of input sequence. Results demonstrated that the model could segment cracks and scales with different sizes accurately. The model performed well in short-term damage prediction. The long-term predictive performance showed decrease than that of short-term, which could be improved by feeding long length of input sequence. The proposed approach demonstrates the feasibility and effectiveness of deep learning-based crack segmentation and damage prediction, which facilitates the move toward real-time analysis and rapid diagnosis of material damage in the future.

Prediction of fatigue–crack growth with neural network-based increment learning scheme

Ultra-low Cycle Fatigue Life Prediction of Stainless Steel Based on Transfer Learning Guided Artificial Neural Network

Prediction of fatigue crack growth under variable amplitude loading by artificial neural network-based Lagrange interpolation

An artificial neural network modeling approach for short and long fatigue crack propagation

Comparative Study of Neural Network–Based Models for Fatigue Crack Growth Predictions of Short Cracks

Image-driven prediction of fatigue crack growth in metal materials via spatiotemporal neural network

Prediction of Fatigue Crack Growth Rate in Aircraft Aluminum Alloys Using Optimized Neural Networks

Predicting the Low‐cycle Fatigue Life of Ti‐6Al‐4V Alloy Using Backpropagation Neural Network Optimized by the Improved Dung Beetle Algorithm

Prediction of Fatigue Crack Damage Using In-Situ Scanning Electron Microscopy and Machine Learning

A physics‐informed neural network framework based on fatigue indicator parameters for very high cycle fatigue life prediction of an additively manufactured titanium alloy

Neural networks for fatigue crack propagation predictions in real-time under uncertainty

Training Deep Neural Networks with Novel Metaheuristic Algorithms for Fatigue Crack Growth Prediction in Aluminum Aircraft Alloys

A new data-driven probabilistic fatigue life prediction framework informed by experiments and multiscale simulation

Study of fatigue crack propagation on modified CT specimens under variable amplitude loadings using machine learning

Comparative Study on Prediction Effects of Short Fatigue Crack Propagation Rate by Two Different Calculation Methods

Prediction of fatigue crack growth using convolutional neural network (2nd Report, Prediction of crack propagation on different levels)

Crack propagation simulation and overload fatigue life prediction via enhanced physics-informed neural networks

A Two‐Scale Model of Fretting Fatigue Crack Initiation Life Based on Long Short‐Term Memory Networks Improved by Genetic Algorithm