Effective elimination of Coomassie Brilliant Blue dye from aqueous solutions using Cerium Metal-Organic Frameworks: Synthesis, characterization, and optimization of adsorption process utilizing Box-Behnken design
Khlood S. Abou-Melha
DOI: https://doi.org/10.1016/j.jwpe.2024.105406
IF: 7
2024-06-01
Journal of Water Process Engineering
Abstract:The study focuses on cerium(III) metal-organic frameworks (Ce-MOFs) as potential adsorbents for the removal of dyes, a major cause of water pollution with serious environmental and public health implications. With several analytical techniques (PXRD, TEM, FESEM, FT-IR, PZC, and XPS), the Ce-MOF microspheres were successfully produced and characterized. The study investigated the potential of Ce-MOF as an adsorbent for the elimination of Coomassie Brilliant Blue (CBB) dye from wastewater. Initially, the synthesized Ce-MOF exhibited impressive physical properties, through a high surface area of 1182.71 m2/g, pore size of 1.47 nm, and pore capacity of 0.87 cm3/g. However, after the adsorption of CBB onto the Ce-MOF, significant changes were observed in these key physical parameters. The surface area decreased to 782.2 m2/g, the pore size reduced to 1.03 nm, and the pore volume dropped to 0.36 cm3/g. These alterations in the physical properties of the Ce-MOF indicate that the dye particles were successfully adsorbed within the porous structure of the adsorbent, effectively occupying the available adsorption sites and reducing the overall surface area, pore size, and pore capacity of the material. Check the effect of the adsorption condition as well as the adsorbent dose, original dye concentration, connection time, and effect of temperature. It was determined that the ideal parameters for attaining a high adsorption capacity were pH 3 and a dosage of 0.02 g. Ce-MOF microspheres have a maximum adsorption capacity of 861.56 mg/g for CBB. Langmuir was fitted from the adsorption isotherm, besides pseudo-second-order was fitted kinetically. Given that the adsorption energy was 26.22 kJ·mol−1, the adsorption method was chemisorption. The resolve of thermodynamic parameters such as ΔG°, ΔH°, ΔS° indicated that the adsorption process was spontaneous as the negativity of ΔG° increased with the rise the temperature, the positive charge of the enthalpy and entropy This designated that the adsorption development was endothermic and randomness. Optimized the results of the adsorption development via Response Surface Methodology and Box-Behnken design (BBD) (RSM). It was suggested that Ce-MOF's adsorption process for CBB dye involved multiple possible mechanisms, such as chemisorption, π-π bonding, pore-filling, electrostatic interactions, and hydrogen bonding, all of which helped remove the dyes from the Ce-MOF material.
engineering, chemical, environmental,water resources