A novel self-degradable gel (SDG) as liquid temporary plugging agent for high-temperature reservoirs

Chenwei Zou,Caili Dai,Yifei Liu,Qing You,Fei Ding,Yongping Huang,Ning Sun
DOI: https://doi.org/10.1016/j.molliq.2023.122463
IF: 6
2023-07-04
Journal of Molecular Liquids
Abstract:In recent years, the liquid temporary plugging agent has drawn extensive attention, especially in the repeated fracturing operation for stimulating unconventional oil and gas reservoir production. This paper developed a novel self-degradable gel (SDG) as a liquid temporary plugging agent for high-temperature reservoirs. The gelation process, viscoelasticity, pressure-bearing capacity, self-degradation, and formation protection performance of the SDG were systematically investigated. Moreover, the gelation and self-degradation mechanism of the SDG were revealed by studying the viscosity variation and the microstructures. Considering the gelation time and gel strength, the composition of the SDG was optimized as 6.0–10.0 wt% monomer, 0.004–0.012 wt% initiator, and 0.2–0.4 wt% crosslinker. The SDG transformed from liquid to solid-like gel within 30 to 90 min at 90–130 °C. The rheological results showed that the duration of the low viscosity state exceeded 75 % of the total gelation process at high temperatures, which was conducive to the injection of the SDG. In addition, the viscosity of the SDG after gelation was more than 100 Pa·s, which ensured its effective plugging in fractures. The experimental results with fractured cores showed that the bearing pressure of the SDG remained above 30 MPa/m in fracture with a width of 2.05–5.04 mm, which could meet the requirements of the repeated fracturing operation. Moreover, the SDG could spontaneously degrade from solid-like gel to liquid with a viscosity of lower than 10 mPa·s in 10–105 h at 90–130 °C. The broken-gel liquid could be completely displaced out of the fractured core, and the core damage rate was less than 5.0 %, which ensured the restoration of conductivity of the previously existing fractures. Micrographs showed that the dense three-dimensional network structure with high viscosity was formed by polymerization and crosslinking. Then, the acrylic acids in the polymer chain were broken at high temperatures, resulting in the gradual destruction of the gel and the spontaneous degradation of SDG.
chemistry, physical,physics, atomic, molecular & chemical
What problem does this paper attempt to address?
This paper attempts to solve the problems faced by the use of temporary plugging agents in repeated fracturing operations in high - temperature reservoirs. Specifically, the paper focuses on developing a new self - degradable gel (SDG) as a liquid temporary plugging agent for high - temperature reservoirs. This SDG needs to have the following characteristics: 1. **Delayed Gelation**: Maintain a low - viscosity state during the injection process to ensure that it can be smoothly injected into the formation fractures. 2. **Stability at High Temperatures**: Be able to form a stable gel under high - temperature conditions to ensure an effective plugging effect. 3. **Spontaneous Degradation**: After completing the plugging task, be able to spontaneously degrade into a low - viscosity liquid at high temperatures, so as to be easily discharged from the formation and restore the conductivity of the fractures. ### Main Problems - **Limitations of Traditional Temporary Plugging Agents**: - Although solid temporary plugging agents (S - TPA) have high strength, they have poor injectability and are difficult to match the size of formation fractures. - Although liquid temporary plugging agents (L - TPA) are easy to inject, the gelation time and degradation process under high - temperature conditions are difficult to control, which may lead to plugging failure or formation pollution. - **Special Requirements of High - Temperature Reservoirs**: - Fracturing operations in high - temperature reservoirs require temporary plugging agents to remain stable at high temperatures and be able to degrade rapidly after completing the plugging, so as to avoid long - term effects on the formation. ### Solutions - **Develop a New Self - Degradable Gel (SDG)**: - Optimize the concentrations of monomers, initiators and cross - linkers to make SDG have the characteristics of delayed gelation and spontaneous degradation at high temperatures. - Systematically study the gelation performance, viscoelasticity, pressure - bearing capacity and formation protection performance of SDG to ensure its effectiveness and safety in practical applications. ### Experimental Methods - **Material Preparation**: Use acrylamide (AM), acrylic acid (AA), N,N' - methylene bisacrylamide (MBA) and tert - butyl hydroperoxide (TBHP) and other raw materials to prepare SDG. - **Gelation Performance Testing**: Evaluate the gelation time and gel strength of SDG by the bottle test method and GSC strength code. - **Rheological Measurement**: Use a rheometer to measure the viscosity change during the gelation process of SDG and the viscoelastic modulus after gelation. - **Pressure - Bearing Capacity Experiment**: Test the pressure - bearing capacity of SDG through an experimental device simulating formation fractures. - **Scanning Electron Microscope (SEM) Measurement**: Observe the microstructure of SDG to reveal its gelation and self - degradation mechanisms. - **Formation Protection Performance Evaluation**: Evaluate the formation protection effect of SDG after degradation by measuring the formation damage rate. ### Results and Discussion - **Gelation Performance**: - When the monomer concentration is in the range of 6.0 - 10.0 wt%, the gelation time of SDG is moderate and the gel strength is high. - When the initiator concentration is in the range of 0.004 - 0.012 wt%, the gelation time of SDG is controllable and the gel strength is stable. - When the cross - linker concentration is in the range of 0.2 - 0.4 wt%, SDG can form a high - strength gel and can completely restore the conductivity of the formation after degradation. - When the temperature is in the range of 90 - 130 °C, the gelation time of SDG is moderate, which is suitable for on - site applications. - **Rheological Characteristics**: - SDG maintains a low - viscosity state most of the time during the gelation process, which is beneficial for injection into the formation. - The viscosity increases sharply in the later stage of gelation, ensuring effective plugging in the fractures. - By adjusting the mass ratio of AM and AA, the elastic modulus and viscous modulus of SDG can be balanced to optimize its plugging effect. - **Pressure - Bearing Capacity and Formation Protection Performance**: - The pressure - bearing capacity of SDG in the fractures exceeds 30 MPa/m, meeting the requirements of repeated fracturing. - The degraded SDG can be completely discharged from the formation, and the formation damage rate is less than 5.0%, ensuring the restoration of the formation's conductivity. In conclusion, through systematic research and optimization, this paper has successfully developed a new self - degradable gel (SDG) suitable for high - temperature reservoirs, solving the challenges faced by traditional temporary plugging agents when used under high - temperature conditions.