Fuhai Li,Gengyuan Liu,Menghui Liu,Zongchi Yang,Zhao Chen,Tao Wen,Jian Guo,Junhu Shao
Abstract:Stud plays an important role in the connection of steel-concrete composite bridge (SCCB). The stud is under pull-out load in the negative moment zone of SCCB. Engineered Cementitious Composites (ECC) are a new type of materials with tensile strain hardening and multiple cracking behavior to strengthen SCCBs. In this study, the cyclic pull-out effect on the ECC-stud connection was studied through pull-out tests. The stud diameter ( d =13/16 mm) and the embedment depth ( h ef =40/60/80 mm) are included as design parameters, resulting in a total of 18 specimens of six scenarios. The failure mode, load-bearing capacity, and ductility factor of the specimens under cyclic loading are compared with those under monotonic loading, and the stiffness, energy dissipation capacity, and residual displacement of the specimens under cyclic loading are analyzed. Based on the experimental results, under cyclic loading, the concrete cone failure and splitting failure occur, and the threshold of h ef / d between the two failure modes is 3.75–4.62, which is smaller than the threshold of the monotonic scenarios. Both concrete and splitting failure modes show ductile failure characteristics because of the bridging effect of fibers in ECC. The load-bearing capacity and ductility factor under cyclic loading are lower than those under monotonic load. This is because, under cyclic loading, the specimens show cumulative damage, which, however, is weakened due to the strengthening effect of ECC. As d and h ef increase, the load-bearing capacity, ductility factor, stiffness, and energy dissipation capacity increase correspondingly, and the residual displacement decreases. The stud with a larger d shows a more obvious ductility holding stage.
construction & building technology,materials science, multidisciplinary,engineering, civil
What problem does this paper attempt to address?
### Problems the Thesis Aims to Solve
This paper aims to study the influence of using engineered cementitious composites (ECC) on the pull - out performance of studs in steel - concrete composite bridges (SCCB). Specifically, through pull - out tests under cyclic loading, the paper explores the influence of ECC on the connection performance of studs. The main research contents include:
1. **Failure Modes of Studs**: Analyze the failure modes of studs with different diameters and embedment depths in ECC under cyclic loading.
2. **Bearing Capacity and Ductility Coefficient**: Compare the bearing capacity and ductility coefficient of studs under cyclic loading and monotonic loading.
3. **Stiffness, Energy Dissipation Capacity and Residual Displacement**: Analyze the changes in the stiffness, energy dissipation capacity and residual displacement of studs under cyclic loading.
### Background and Motivation
In steel - concrete composite bridges (SCCB), studs bear pull - out loads in the negative moment area, and their pull - out performance is a key consideration in design and construction. Traditional concrete materials are prone to cumulative damage under cyclic loading, resulting in performance degradation. As a high - performance fiber - reinforced cementitious composite, ECC has tensile strain - hardening and multi - cracking behaviors, which can improve the durability and self - healing ability of the structure. Therefore, studying the influence of ECC on the pull - out performance of studs under cyclic loading is of great significance for improving the reliability and durability of SCCB.
### Research Methods
1. **Materials and Test Methods**:
- Use PVA - fiber - reinforced ECC as the base material.
- Design stud specimens with different diameters (13mm and 16mm) and embedment depths (40mm, 60mm and 80mm).
- Adopt the displacement - controlled loading method for monotonic loading and cyclic loading tests.
2. **Test Scheme**:
- Prepare cylindrical ECC specimens with a diameter of 270mm and a height of 120mm, with studs pre - embedded in the center.
- Conduct pull - out tests through a custom - made loading frame device.
- Cyclic loading is divided into two stages: pre - loading and formal loading. The formal loading adopts the displacement - controlled loading method, and the target force of each loading level gradually increases.
### Main Results
1. **Failure Modes**:
- In ECC, the failure modes of studs mainly include concrete cone failure and concrete splitting failure.
- When the embedment depth - to - diameter ratio (hef/d) is less than 3.75, it mainly shows concrete cone failure; when hef/d is greater than 4.62, it mainly shows concrete splitting failure.
2. **Bearing Capacity and Ductility Coefficient**:
- Under cyclic loading, the bearing capacity and ductility coefficient of studs are both lower than those under monotonic loading.
- With the increase in stud diameter and embedment depth, the bearing capacity and ductility coefficient increase accordingly.
3. **Stiffness, Energy Dissipation Capacity and Residual Displacement**:
- Under cyclic loading, the stiffness and energy dissipation capacity of studs decrease, but the enhancement effect of ECC partially weakens this decrease.
- With the increase in stud diameter and embedment depth, the stiffness and energy dissipation capacity increase, and the residual displacement decreases.
### Conclusions
As a high - performance material, ECC can significantly improve the pull - out performance of studs under cyclic loading, especially the ductility characteristics. However, due to the cumulative damage caused by cyclic loading, the bearing capacity and stiffness of studs will still decrease to some extent. These research results provide an important reference basis for the design and construction of SCCB.