Abstract:Beaded activated carbons (BACs) were derived from waste bamboo tar through carbonization (500°C for 2 hr) followed by physical activation using carbon dioxide (800–900°C for 2–4 hr). The adsorbent was examined for their physical and chemical properties, adsorption capacities toward methylethylketone (MEK) and toluene, and regenerabilities under microwave heating. It was found that the maximum total surface area reached for bamboo-tar-derived BAC after physical activation was 1364 m2 g−1, and more than 95% of the area was attributed to the microporous structures. Langmuir, Freundlich, and Dubinin-Radushkevich (D-R) isotherm models were applied to the adsorption isotherm fitting, and the minimum R2 for each model was 0.986, 0.915, and 0.943, respectively. The isosteric heats of adsorption calculated based on D-R parameters for methylethylketone and toluene were 44.04 to 51.50 and 45.88 to 73.27 KJ mol−1, respectively. They were slightly over the range of physisorption and increased with adsorbate loading, which might be related to the micropore filling mechanism. Microwave regeneration under 600 W of power output removed most of the adsorbate (>93.03%) within 8 min. The results of this study are intended to benefit future study on waste-derived adsorbent in environmental applications.Recycling waste bamboo tar for the novel adsorbent preparation is shown feasible in this study. Beaded activated carbon (BAC) synthesized from this waste bamboo tar possessed a high specific surface area, which aided in the capturing of volatile organic compounds (VOCs). Three adsorption isotherms, Langmuir, Freundlich, Dubinin-Radushkevich (D-R) models can be applied in interpreting the experimental adsorption data, providing information on adsorption heat and possible adsorption mechanism. A potential microwave regeneration method for BAC is tested, showing high desorption efficiencies with minimum heel formation. These findings can provide a new pathway for waste bamboo tar management and VOC abatement using adsorbents.

Preparation of activated carbon from ginkgo leaves by steam activation for adsorption application with isotherm and kinetics

Activated carbon from Myrica rubra (Chinese bayberry) stones using steam preparation and its adsorption capabilities

Optimizing the Desorption Technology of Total Flavonoids of Ginkgo Biloba from Separating Materials of Activated Carbon

Activated Carbon Derived from Carbon Residue from Biomass Gasification and Its Application for Dye Adsorption: Kinetics, Isotherms and Thermodynamic Studies.

Enhancing graphitization with desirable porosity for CO 2 adsorption through a one-step strategy and a novel stepwise pyrolysis method from Terminalia boivinii tul tree dead leaves

Adsorption of Pb(II) and Cu(II) by Ginkgo-Leaf-Derived Biochar Produced under Various Carbonization Temperatures and Times

Hierarchical Pore Structure of Activated Carbon Fabricated by CO2/microwave for Volatile Organic Compounds Adsorption

Sustainable activated carbons from dead ginkgo leaves for supercapacitor electrode active materials

Preparation of Activated Carbon Adsorption Materials Derived from Coal Gasification Fine Slag Via Low-Temperature Air Activation

Preparation of activated carbon through the pyrolysis of waste bamboo chips and evaluation of its CO2 adsorption efficacy

Preparation And Characterization Of Activated Carbon From Kraft Lignin Via Koh Activation

Activated carbon from biomass waste precursors: Factors affecting production and adsorption mechanism

Preparation, characterization and adsorption performance of high surface area biomass-based activated carbons

Utilization of Biomass Waste for Activated Carbon Production by Steam Gasification in a Rotary Reactor: Experimental and Theoretical Approach

Porous and high specific surface area carbon material derived from ginkgo leaves for high-performance symmetric supercapacitors

Preparation of Porous Activated Carbon with Ultra-High Specific Surface Area and Its Adsorption Performance for Specific Organic Pollutants in Industrial Wastewater

Activated carbon preparation from eucalyptus wood chips using continuous carbonization–steam activation process in a batch intermittent rotary kiln

Preparation of High Specific Surface Area and High Adsorptive Activated Carbon by KOH Activation

Procedure optimizations and characterizations of new-type high-efficient activated carbon used in drinking water purification

Effect of Acid and Hydrothermal Treatments on the Dye Adsorption Properties of Biomass-Derived Activated Carbon

Comprehending adsorption of methylethylketone and toluene and microwave regeneration effectiveness for beaded activated carbon derived from recycled waste bamboo tar