Development and evaluation of nitride coated titanium bipolar plates for PEM fuel cells

Jun Bi,Jinmeng Yang,Xiaoxiang Liu,Dongdong Wang,Zhaoyi Yang,Gaoyang Liu,Xindong Wang
DOI: https://doi.org/10.1016/j.ijhydene.2020.09.217
IF: 7.2
2021-01-01
International Journal of Hydrogen Energy
Abstract:<p>In order to improve the conductivity of titanium bipolar plate under the premise of ensuring its corrosion resistance for the proton exchange membrane fuel cell (PEMFC), the nitride coatings are deposited on the surface of titanium bipolar plate via a powder immersion reaction assisted coating (PIRAC) method. Both the scanning electron microscopy (SEM) and energy dispersive spectrometer (EDS) show that the dense titanium nitride coatings with the thickness around 1.5–2.5 μm are successfully prepared. Furthermore, the X-ray photoelectron spectroscopy (XPS) results confirm the presence of TiN, TiN<sub>x</sub>O<sub>y</sub> and TiO<sub>2</sub> phases on the surface of nitride coatings, and the content of these phases is tunable by adjusting the prepared temperatures. Both the microstructure, the thickness and the composition of the nitride coatings could be associated with the corrosion resistance and the interfacial contact resistance of the nitrided samples. We find that the nitrided samples prepared at 1000 °C could be the ideal mixed coating materials with the proper combination of the corrosion resistance and the interfacial contact resistance, which also show the best long-term stability in simulated PEMFC cathode environment.</p>
energy & fuels,electrochemistry,chemistry, physical
What problem does this paper attempt to address?
### Problems the paper attempts to solve This paper aims to improve the electrical conductivity of titanium bipolar plates (BPs) in proton exchange membrane fuel cells (PEMFCs) while ensuring their corrosion resistance. Specifically, researchers deposit nitride coatings on the surface of titanium bipolar plates through the Powder Immersion Reaction Assisted Coating (PIRAC) method to enhance their overall performance in PEMFCs. ### Main problems and solutions 1. **Corrosion resistance problem**: - Although titanium materials have relatively good corrosion resistance, their surfaces are prone to oxidize and form oxide films with low electrical conductivity, thereby increasing the interfacial contact resistance (ICR). - Researchers deposit titanium nitride (TiN) coatings on the surface of titanium bipolar plates through the PIRAC method to improve their corrosion resistance. The experimental results show that the nitride coatings significantly improve the corrosion resistance of titanium bipolar plates. In particular, the samples prepared at 1000°C perform the best, with a corrosion current density of only 0.009 mA/cm², far below the target value (<1 mA/cm²) of the US Department of Energy (DOE). 2. **Electrical conductivity problem**: - The oxide films with low electrical conductivity will increase the interfacial contact resistance between the titanium bipolar plates and the diffusion layer, affecting the performance of PEMFCs. - The nitride coatings not only improve the corrosion resistance of titanium bipolar plates but also significantly reduce their interfacial contact resistance. For the samples prepared at 1000°C, under a compressive force of 140 N/cm², the ICR is only 4.6 mΩcm², far lower than that of the untreated titanium substrate (75.9 mΩcm²). 3. **Long - term stability problem**: - The working environment of PEMFCs is strongly acidic and has a high potential, which is likely to cause material corrosion. - Researchers verify the long - term stability of the nitride coatings through long - term stability tests (LTST) simulating the cathode environment of PEMFCs. The results show that after 12 hours of LTST, the samples prepared at 1000°C still maintain good corrosion resistance and electrical conductivity. ### Conclusion Depositing nitride coatings on the surface of titanium bipolar plates through the PIRAC method can significantly improve their corrosion resistance and electrical conductivity and also has good long - term stability. In particular, the samples prepared at 1000°C achieve the optimal performance and meet the strict requirements of PEMFCs for bipolar plate materials. This research result provides a new solution for the application of titanium bipolar plates in PEMFCs.