Abstract:<p>A hyperbranched polyamide charring agent (HPCA) was synthesized by amidation of 1,2,3,4-butanetetracarboxylic acid and melamine, and its chemical structure was characterized. Such a charring agent, combined with ammonium polyphosphate (APP), was applied in epoxy resin. V-0 rating in the UL-94 vertical burning test and 32.3% of Limiting Oxygen Index were achieved with only 10% total flame retardant loading. A HPCA/APP ratio of 1/1 showed better flame retardant properties than the system with only HPCA or APP involved, indicating an apparent synergistic effect. The residual char at high temperature was analyzed by using FTIR and X-ray Photoelectron spectroscopy (XPS) to further explore the above synergistic mechanisms. Additionally, HPCA, as a co-curing agent, was grafted into the crosslinking net of epoxy resin due to the reactivity of carboxylic acids with epoxy group and hydroxyl group. The introduced hyperbranched polyamide structure effectively improved the toughness of original rigid crosslinking net of epoxy resin.</p>

What problem does this paper attempt to address?

The paper mainly addresses the following issues: 1. **Development of a new efficient flame retardant**: The research team synthesized a hyperbranched polyamide char-forming agent (HPCA) aimed at improving the flame retardancy of epoxy resin (EP). Traditional char-forming agents have problems such as low decomposition temperature, poor water stability, and low flame retardant efficiency. Therefore, developing an efficient char-forming agent is of great significance. 2. **Improving the flame retardancy and toughness of epoxy resin**: By combining HPCA with ammonium polyphosphate (APP), the epoxy resin achieved good flame retardant effects (UL-94 V-0 rating) with a lower addition amount. Additionally, HPCA also participated as a co-curing agent in the curing process of epoxy resin, effectively enhancing the toughness of the material. 3. **Exploring the synergistic flame retardant mechanism**: The synergistic mechanism between HPCA and APP was studied, revealing that they can form stable cross-linked residues at high temperatures, promoting the formation of a dense and thermally stable char layer, further improving the flame retardancy of the epoxy resin. 4. **Evaluating material performance**: Through vertical burning tests, limiting oxygen index tests, cone calorimeter tests, etc., the excellent flame retardant effect and smoke suppression ability of the HPCA and APP composite system in epoxy resin were verified. Meanwhile, mechanical performance tests were conducted to evaluate the impact of HPCA on the toughness of epoxy resin. In summary, this study successfully synthesized a new type of hyperbranched polyamide char-forming agent and experimentally verified its significant effects on improving the flame retardancy and toughness of epoxy resin. This work is of great value for the development of high-performance flame retardant epoxy resin materials.

Synthesis of a hyperbranched polyamide charring agent and its flame-retarding and toughening behavior in epoxy resin

Synthesis of a Novel Hyperbranched and Phosphorus‐containing Charring‐foaming Agent and Its Application in Polypropylene

One-pot Synthesis of a Novel S-Triazine-based Hyperbranched Charring Foaming Agent and Its Enhancement on Flame Retardancy and Water Resistance of Polypropylene

Flame Retardancy and Thermal Properties of Novel Uv-Curable Epoxy Acrylate Coatings Modified by A Silicon-Bearing Hyperbranched Polyphosphonate Acrylate

Synthesis of A Novel Charring Agent Containing Pentaerythritol and Triazine Structure and Its Intumescent Flame Retardant Performance for Polypropylene

Synthesis of a charring-foaming agent containing triazine and triazole groups and its flame retardancy in PP

Flame Retardancy and Thermal Property of Novel Uv-Curable Epoxy Acrylate Coatings Modified by Melamine-Based Hyperbranched Polyphosphonate Acrylate

Synthesis of a highly efficient charring agent and its application to intumescent flame‐retardant coatings for 3D‐printed polypropyleneparts

An efficient flame retardant for epoxy resin: Preparation and pyrolytic behaviour

Novel Multifunctional Organic–Inorganic Hybrid Curing Agent with High Flame-Retardant Efficiency for Epoxy Resin

Synthesis of a Novel Triazine-Based Hyperbranched Char Foaming Agent and the Study of Its Enhancement on Flame Retardancy and Thermal Stability of Polypropylene

Facile Synthesis of a Novel Hyperbranched Poly(urethane-Phosphine Oxide) As an Effective Modifier for Epoxy Resin

A boron‐containing ammonium polyphosphate for epoxy resins with enhanced flame retardancy and reduced smoke release

Microencapsulated Ammonium Polyphosphate with Glycidyl Methacrylate Shell: Application to Flame Retardant Epoxy Resin

Synthesis of a hyperbranched phosphorus-containing polyurethane as char forming agent combined with ammonium polyphosphate for reducing fire hazard of polypropylene

Synthesis of a triazine charring agent containing hydroxyl and triazine ring and its flame retardant application in thermoplastic polyolefin

A hyperbranched P/N/B-containing oligomer as multifunctional flame retardant for epoxy resins

Synthesis of bio‐based reactive N/P flame retardant and its curing and flame retarding behavior in epoxy resins

Piperazine polypyrophosphat-halloysite panotubes-melamine cyanurate synergistic flame retardant epoxy resin br

An improved intumescent flame-retardant epoxy resin with hydroxylated melamine as both charring and blowing agent

Synthesis of Hyperbranched Flame Retardants with Varied Branched Chains' Rigidity and Performance of Modified Epoxy Resins