Piperazine polypyrophosphat-halloysite panotubes-melamine cyanurate synergistic flame retardant epoxy resin br

Jing Ma,Meizhe Liu,Mingxuan Zhu,Jing Zhu,Zhaobang Zhang,Baohe Wang

DOI: https://doi.org/10.11868/j.issn.1001-4381.2022.000243

2023-01-01

Journal of Materials Engineering

Abstract:By improving the existing preparation methode. a piperazine polypyrophosphat (PAPP) with igh thermal stability was synthesized. It was compounded with helloysite nanotube (HNTs) and Melamine cyanurate (MCA) to form P-N-51 intumescent flame retardant, and was used in synergistic Hame retardant epoxy resin (EP). The effect of intumescent flame retardant on the flame retardancy of EP was investigated by means of limiting oxygen index, vertical combustion, cone calorimeter and EM . The results show that the introduction of the compound flame retardant forms a dense and Jontinuous intumescent carbon layer, which improves the flame retardant efficiency of the epoxy resin the condensed phase and the gas phase. It reduces the heat release and heat release rate of epoxy Jesin and the toxic gases release effectively. When the PAFF HNT/MCA ratio is 7112, the miting oxygen index of flame retardant resin reaches 34. 3%, the UL-94 vertical combustion test seaches V-0 level. Compared with pure EF, the amount of residual carbon is increased significantly, the peak heat release rate (HRR) is decreased by 50.55%, and the total heat release (THR) and toxic es emissions are reduced significantly for modified EP. In addition, the thermogravimetric analysis Results suggest that the initial decomposition temperature of flame retardant modified EP is decreased br 4.4% (A7), and the modified EP still has high thermal stability.