Abstract:This study investigates the corrosion behavior of Ni-Cr binary alloys, including Ni-10Cr, Ni-15Cr, Ni-20Cr, Ni-25Cr, and Ni-30Cr, in a NaCl-KCl-MgCl2 molten salt mixture through gravimetric analysis. Corrosion tests were conducted at 700 °C, with the maximum immersion time reaching up to 100 h. The corrosion rate was determined by measuring the mass loss of the specimens at various time intervals. Verifying corrosion rates by combining mass loss results with the determination of element dissolution in molten salts using Inductively Coupled Plasma Optical Emission Spectroscopy (ICP-OES). Detailed examinations of the corrosion products and morphology were conducted using X-ray diffraction (XRD) and scanning electron microscopy (SEM). Micro-area elemental analysis on the corroded surfaces was performed using an energy dispersive spectrometer (EDS), and the elemental distribution across the corrosion cross-sections was mapped. The results indicate that alloys with lower Cr content exhibit superior corrosion resistance in the NaCl-KCl-MgCl2 molten salt under an argon atmosphere compared to those with higher Cr content; no corrosion products were retained on the surfaces of the lower Cr alloys (Ni-10Cr, Ni-15Cr). For the higher Cr alloys (Ni-20Cr, Ni-25Cr, Ni-30Cr), after 20 h of corrosion, a protective layer was observed in certain areas. The formation of a stable Cr2O3 layer in the initial stages of corrosion for high-Cr content alloys, which reacts with MgO in the molten salt to form a stable MgCr2O4 spinel structure, provides additional protection for the alloys. However, over time, even under argon protection, the MgCr2O4 protective layer gradually degrades due to chloride ion infiltration and chemical reactions at high temperatures. Further analysis revealed that chloride ions play a pivotal role in the corrosion process, not only facilitating the destruction of the Cr2O3 layer on the alloy surfaces but also possibly accelerating the corrosion of the metallic matrix through electrochemical reactions. In conclusion, the corrosion behavior of Ni-Cr alloys in the NaCl-KCl-MgCl2 molten salt environment is influenced by a combination of factors, including Cr content, chloride ion activity, and the formation and degradation of protective layers. This study not only provides new insights into the corrosion resistance of Ni-Cr alloys in high-temperature molten salt environments but also offers significant theoretical support for the design and optimization of corrosion-resistant alloy materials.

High‐temperature KCl‐induced corrosion of high Cr and Ni alloys investigated by in‐situ diffraction

Effect of KCl on high‐temperature corrosion of low‐alloyed steel under low oxygen partial pressure

Influence of KCl and HCl on a Laser Clad FeCrAl Alloy: In-Situ SEM and Controlled Environment High Temperature Corrosion

Cr diffusion coatings on a ferritic-martensitic steel for corrosion protection in KCl-rich biomass co-firing environments

Corrosion characteristics of Inconel 625 cladding layer and NiCrMoAl cladding layer in molten NaCl-KCl and NaCl-KCl-Na 2 SO 4

Corrosion Behavior of Ni-Cr Alloys with Different Cr Contents in NaCl-KCl-MgCl2

Corrosion behavior of AlCoCrFeNi2.1 eutectic high-entropy alloy in Cl--containing solution

Corrosion Behavior of the AlCoCrFeNi2.1 Eutectic High-Entropy Alloy in Chloride-Containing Sulfuric Acid Solutions at Different Temperatures

Study of KCl-induced hot corrosion behavior of high velocity oxy-fuel sprayed NiCrAlY and NiCrBSi coatings deposited on 12CrMoV boiler steel at 700 °C

Corrosion Behavior of As-Cladding Al 0.8 CrFeCoNiCu 0.5 Si x High Entropy Alloys in 3.5% NaCl Solution

Corrosion Behavior of the GH3535 and C276 Alloys at the Liquid/Gas LiCl–KCl Salt Interface at 550 °C

In situ Bragg coherent X-ray diffraction imaging of corrosion in a Co-Fe alloy microcrystal

Corrosion Behavior of Ultrafine-Grained CoCrFeMnNi High-Entropy Alloys Fabricated by High-Pressure Torsion

Visualizing time-dependent microstructural and chemical evolution during molten salt corrosion of Ni-20Cr model alloy using correlative quasi in situ TEM and in situ synchrotron X-ray nano-tomography

The Influence of the Composition of Amorphous Alloys on Their Corrosion Resistance in Aggressive Environments of Different Nature

Corrosion Behavior of Nitrogen-Containing Low-Nickel Weld Cladding in KCl-MgCl2 Eutectic Molten Salt at 900 °C

The characterization of corrosion layers of GH3535 and Inconel 625 alloys in molten KNO3-NaNO3 salts at 500 °C

The effect of thermal-induced phase transformation on the corrosion behavior of Inconel 625 alloy in NaCl-KCl-MgCl 2 molten salt

Corrosion behavior of Ni–25Cr–10Fe–3Si–xMo alloys beneath KCl–ZnCl2 deposits at 650°C: Role of long‐term aging

An experimental high-throughput to high-fidelity study towards discovering Al-Cr containing corrosion-resistant compositionally complex alloys

Effect of Cryogenic Laser Surface Modification on the Microstructure Evolution and Corrosion Resistance of Accident-Tolerant FeCrAl Alloys