Tuning ferroelectric domains and polarization properties of flexible BiFeO 3 thin films by phase transition engineering
Jia He,Shibing Xiao,Huiting Sui,Fuling Wu,Xiao Li,Cheng Yang,Piyu Gong,Jianing Zhu,Xiaofang Liu,Huajun Sun
DOI: https://doi.org/10.1016/j.jallcom.2024.176756
IF: 6.2
2024-10-02
Journal of Alloys and Compounds
Abstract:In the present investigation, thin films of flexible (Bi 1-x Sm x )(Fe 0.95 Mn 0.05 )O 3 (denoted as BSFM0, BSFM4, BSFM8, and BSFM12 for x=0 %, 4 %, 8 %, and 12 %, respectively) were synthesized on metallic Ni-Cr substrates via the sol-gel technique. A comprehensive examination was conducted to elucidate the influence of varying concentrations of Sm 3+ substitution on the phase constitution, oxygen vacancy concentration, and leakage behavior of the (Bi 1-x Sm x )(Fe 0.95 Mn 0.05 )O 3 films. Utilizing X-ray diffraction (XRD) and Raman spectrometry, it was ascertained that all films exhibited a composite structure comprising orthorhombic (Pnma) and rhombohedral (R3c) phases. An augmentation in Sm 3+ doping led to a non-monotonic variation in the R3c phase content, initially increasing and subsequently decreasing, while the nonpolar Pnma phase demonstrated a progressive enhancement. The distorted R3c phase was found to promote the flipping of the domain architecture, thereby augmenting the polarization attributes. Notably, at a Sm doping level of 4 %, the maximum polarization ( P max ) attained was 95 μC/cm 2 , with a remnant polarization ( P r ) of 78 μC/cm 2 . The incorporation of a judicious amount of Sm was observed to curtail film leakage and decelerate the aging phenomenon. The compositional stability of this doping level was evaluated across a frequency spectrum of 0.1–12 kHz and a temperature gradient of 25–200 °C, revealing no propensity for degradation under conditions of polarization, a holding duration of 10 4 s, or fatigue scenarios involving a curvature of 5 mm and 10 8 switching cycles subjected to 10 3 instances of bending. These findings provide innovative insights for the development of next-generation lead-free transducer apparatus and flexible information storage mediums.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering