Abstract:Zwitterionic polysulfone (PSf) ultrafiltration membranes were fabricated by non-solvent phase separation (NIPS) method. Herein, a casting solution at 45 °C was developed by using chloromethylated polysulfone (CMPSf), N, N-dimethylacetamide (DMAc) as a solvent, 4-amino-benzenesulfonic acid monosodium salt (ABS) as a cross-linking agent, and Na 2 CO 3 as an acid binder. Simultaneously, the occurrence of the electrophilic substitution reaction between ABS and CMPSf caused the formation of ABS grafting CMPSf (CMPSf-g-ABS). After a specific reaction time, the casting solution was applied to cast membranes, which were subsequently submerged in coagulation bath. A zwitterionic ultrafiltration (ZUF) membrane was obtained using NIPS following the treatment of hydrochloric acid (HCl) solution (1 M mol). Because of the formation of cross-linked CMPSf-g-ABS, the results revealed that the casting solution's viscosity increased sharply from 425.4 mPa s at the initial stage (0 h) to 4810.8 mPa s (22 h). Interestingly, the morphology of the membranes with an asymmetric finger-like structure at 0 h gradually transformed to a gradient sponge-like structure after 22 h. Specifically, the ZUF membrane (M22-H) with the gel fraction of 72.1% procured after the reaction of 22 h demonstrated a low water contact angle (40.17°) and a high pure water permeance (420.4 L m −2 h −1 bar −1 ). The M22-H also exhibited a high flux recovery rate (FRR) (90.2%), bovine serum albumin (BSA) rejection (>95%), and Escherichia coli ( E. coli ) antibacterial rate (96.2%). The surface of the ZUF membrane with numerous zwitterionic groups enhances the hydration layer's energy (i region 16 nm), causing a significant improvement in the antifouling performance. This research opens new avenues for preparing zwitterionic functional membranes.

Inhibition of biofouling by in-situ grown zwitterionic hydrogel nanolayer on membrane surface in ultralow-pressurized ultrafiltration process

Zwitterion-like, Charge-Balanced Ultrathin Layers on Polymeric Membranes for Antifouling Property.

Enhanced Antifouling Capability of In Situ- Grown Hydrophilic-Hydrophobic Nanodomains on Membrane Surface in the Ultralow Pressurized Ultrafiltration Process

Antifouling and Antibacterial Behavior of Membranes Containing Quaternary Ammonium and Zwitterionic Polymers

Fouling Resistance of 3-[[3-(trimethoxysilane)-propyl] Amino] Propane-1-sulfonic Acid Zwitterion Modified Poly (vinylidene Fluoride) Membranes

A novel membrane showing both hydrophilic and oleophobic surface properties and its non-fouling performances for potential water treatment applications

Preparation and Characterization of an Amphiphilic Polyamide Nanofiltration Membrane with Improved Antifouling Properties by Two-Step Surface Modification Method

Azido-group Functionalized Graphene Oxide/polysulfone Mixed Matrix Ultrafiltration Membrane with Enhanced Interfacial Compatibility for Efficient Water and Wastewater Treatment

Guanidyl-functionalized Graphene/polysulfone Mixed Matrix Ultrafiltration Membrane with Superior Permselective, Antifouling and Antibacterial Properties for Water Treatment

Membrane surface coated with zwitterions for fouling mitigation in membrane bioreactor: Performance and mechanism

Stimuli-Responsive Lysozyme Nanocapsule Engineered Microfiltration Membranes with a Dual-Function of Anti-Adhesion and Antibacteria for Biofouling Mitigation

Polyhydroxy Group Functionalized Zwitterion for a Polyamide Nanofiltration Membrane with High Water Permeation and Antifouling Performance

Simple and Effective Preparation of Zwitterionic Anti‐Fouling Poly(vinylidene fluoride) Ultrafiltration Membrane by In Situ Cross‐Linking Polymerization Technology

Facile plasma grafting of zwitterions onto nanofibrous membrane surface for improved antifouling properties and filtration performance

Preparation of novel zwitterionic polysulfone ultrafiltration membranes for the dual-enhanced antifouling and antibacterial properties by in-situ one pot crosslinking reaction

Molecular design of antifouling ultrafiltration membranes via copolymerization of bactericidal and hydrophilic polymers

Antifouling Fibrous Membrane Enables High Efficiency and High-Flux Microfiltration for Water Treatment

Surface modification of FeⅢ-juglone coating on nanofiltration membranes for efficient biofouling mitigation

Facile preparation of antifouling nanofiltration membrane by grafting zwitterions for reuse of shale gas wastewater

Membrane Biofouling Control by Surface Modification of Quaternary Ammonium Compound Using Atom-Transfer Radical-Polymerization Method with Silica Nanoparticle as Interlayer

Reinforcing hydration layer on membrane surface via nano-capturing and hydrothermal crosslinking for fouling reduction