Abstract:Solid-state sodium metal batteries have been proposed as an alternative to lithium-ion batteries (LIBs) for next-generation applications due to the high abundance and wide distribution of sodium resources. 1 Sodium antiperovskites (Na 3 OX, X = Cl, Br, or BH 4 ) have recently attracted great interest as solid electrolyte candidates due to the relatively low processing temperature (<500 o C), reasonable ionic conductivity (up to 4.4 x 10 -3 S cm -1 at room temperature), and great chemical stability against sodium metal anodes. 2,3 Typical solid-state ionic conductors have temperature-dependent ionic conductivity that follows Arrhenius behaviour over a broad range of temperatures, corresponding to a constant activation energy E a . However, this is not the case in Na 3 OBr, and instead a phenomenon resulting in a higher ionic conductivity and lower activation energy is observed to occur at 255 o C. Similar non-Arrhenius ionic conductivity phenomenon has also been reported in the potassium antiperovskite K 3 OI. It has been proposed that this behaviour originated from anion disordering, but conclusive experimental evidence to support this claim has not been reported. 4 An understanding of the origin of this behaviour could enable the synthesis route to be optimised such that higher ionic conductivities could be achieved. In this work, we combined temperature-resolved bulk and local characterisation methods including Pawley and Rietveld refinements of synchrotron x-ray diffraction (XRD), pair distribution function (PDF), solid-state nuclear magnetic resonance (NMR) spectroscopy, and electrochemical impedance spectroscopy (EIS) to gain an insight into the origin of this non-Arrhenius behaviour. We found that this phenomenon does not originate from anion disordering, as previously speculated, because the lattice parameter of Na 3 OBr changed linearly with temperature and no major intensity changes were observed in the Na-Br and Na-O signals in the PDF patterns. Other supporting findings that lead us to this conclusion will be discussed in the presentation. References Wang, X. et al. Ultra-stable all-solid-state sodium metal batteries enabled by perfluoropolyether-based electrolytes. Nat. Mater. 21 , 1057–1066 (2022). Zheng, J., Perry, B. & Wu, Y. Antiperovskite Superionic Conductors: A Critical Review. ACS Mater. Au 1 , 92–106 (2021). Sun, Y. et al. Rotational Cluster Anion Enabling Superionic Conductivity in Sodium-Rich Antiperovskite Na3OBH4. J. Am. Chem. Soc. 141 , 5640–5644 (2019). Zheng, J. et al. Antiperovskite K3OI for K-Ion Solid State Electrolyte. J. Phys. Chem. Lett. 12 , 7120–7126 (2021).

Mean Ionic Activity Coefficients of NaBr in the Ternary System NaBr–SrBr 2 –H 2 O at 288.15 K using the Cell Potential Method

Mean Activity Coefficients of NaBr in Ternary System NaBr–Na 2 SO 4 –H 2 O Determined by the Cell Potential Method at 308.15 K

Average Activity Coefficients of NaBr in the Ternary System NaBr–Na 2 SO 4 –H 2 O Determined by the Cell Potential Method at 318.15 K

Non-Arrhenius Ionic Conductivity Behaviour in Antiperovskite Solid Electrolytes for Sodium Metal Batteries

Thermodynamic Properties of the Ternary System Potassium Bromide + Lithium Bromide + Water at 25°C

Mean activity coefficients of KCl in the KCl + SrCl2 + H2O solutions at 278.15 K determined by cell potential method and their application to the prediction of solid-liquid equilibria of the KCl + SrCl2 + H2O system

Thermodynamic properties of the ternary system (KBr + PEG 4000 + water) by potentiometric method at T = (288.2, 298.2, and 308.2) K

Osmotic and Activity Coefficient of 1-Ethyl-3-methylimidazolium Bromide in Aqueous Solutions of Potassium Dihydrogen Phosphate, Dipotassium Hydrogen Phosphate, and Tripotassium Phosphate at T = 298.15 K

Experiment and Calculation of Solid–Liquid Phase Equilibria in the Ternary System SrCl 2 –SrBr 2 –H 2 O at T = 273, 298, and 323 K

Computational Screening of Na 3 MBr 6 Compounds as Sodium Solid Electrolytes

Activity Coefficients for Nacl in Meoh+H2o by Electromotive Force Measurements at 308.15 K and 318.15 K

Study on thermodynamic properties of aqueous lithium salts

Ionic Conductivity and Ion Association in Aqueous NaCl + Mannitol Solutions at Temperatures from 293.15 to 313.15 K

Sodium Ion Transport Mechanisms in Antiperovskite Electrolytes Na3obr and Na4oi2: an in Situ Neutron Diffraction Study

On Preparation and Conductivity of 1-Hexyl-3-methylimidazolium Bromide

Study on the Phase Equilibrium of the Quaternary Na 2 SO 4 –NaBr–NH 4 Br–(NH 4 ) 2 SO 4 –H 2 O System at 298.15 and 323.15 K

Thermodynamic Properties of Aqueous Mixtures of Licl and Li2so4 at Different Temperatures

Molar Conductance of Sodium Bromide and Sodium Iodide in Methanol + Water at 298.15 K

Individual activity coefficients of chloride ions in aqueous solutions of MgCl2, CaCl2 and BaCl2 at 298.2 K

High ionic conductivity materials Li3YBr6and Li3LaBr6for solid-state batteries: first-principles calculations

Solid–Liquid Phase Equilibria in the Ternary System CaBr 2 –SrBr 2 –H 2 O at 273, 298, and 323 K