Abstract:Phase equilibria and structural transformations in the ternary ZrO2–HfO2–Eu2O3 system at 1100 °C were studied by X-ray diffraction over the entire composition range. The samples of different compositions have been prepared from nitrate acid solutions by evaporation, drying, and calcinations at 1100 °C. Fields of solid solutions based on the cubic (F) modification with fluorite-type structure and tetragonal (T) and monoclinic (M) modifications of ZrO2 (HfO2), cubic (C) modification of Eu2O3, and an ordered intermediate phase with pyrochlore-type structure, Ln2Zr2O7 (Ln2Hf2O7)(Py), were established to exist in the system. The solubility of Eu2O3 in M-HfO2(ZrO2) is pretty low and approximately less than 1 mol%, which is confirmed by XRD. The boundaries of phase fields and lattice parameters of the phases were determined. The lattice parameters for F phase vary from а = 0.5305 nm in two-phase sample (C+F) containing 6.75 mol% ZrO2–8.25 mol% HfO2–85 mol% Eu2O3 to а = 0.5283 nm for sample containing 27 mol% ZrO2–33 mol% HfO2–40 mol% Eu2O3 and to а = 0.5275 nm in two-phase sample (Py+F) containing 29.25 mol% ZrO2–35.75 mol% HfO2–35 mol% Eu2O3, and from а = 0.5232 nm in two-phase sample (Py+F), containing 32.625 mol% ZrO2–39.875 mol% HfO2–27.5 mol% Eu2O3 to а = 0.5218 nm sample containing 33.75 mol% ZrO2–41.25 mol% HfO2–25 mol% Eu2O3 and to а = 0.5176 nm in two-phase sample (F+M) containing 40.5 mol% ZrO2–49.5 mol% HfO2–10 mol% Eu2O3 along the section Eu2O3–(55 mol% HfO2–45 mol% ZrO2). The fluorite-type structure (F) is in equilibrium with all phases that exist in the ternary ZrO2–HfO3–Eu2O3 system at 1100 °C and forms substitutional solid solutions with phases of the binary systems. In the ZrO2–HfO2–Eu2O3 system, an infinite series of solid solutions form from the Ln2Zr2O7 (Ln2Hf2O7) (Py) phase. The isothermal section of the ZrO2–HfO2–Eu2O3 phase diagram at 1100 °C contains one three-phase regions (T + M + F) and six two-phase regions (F + C, two-F + Py, F + M, F + T, T + M). No new phases were found in the ZrO2–HfO2–Eu2O3 system at 1100 °C and the nature of phase equilibria was determined by the constitution of the boundary binary systems.

Phase diagrams of the BaF2–NdF3 and BaF2–PrF3 systems

Fluorite Solid Solutions of Congruent Melting in the PbF2–CdF2–RF3 Systems

PHASE-RELATIONS IN THE SYSTEM BAO-ND2O3-B2O3 (B2O3-GREATER-THAN-OR-EQUAL-TO-50 MOL-PERCENT) AND CRYSTAL-GROWTH OF NDBAB9O16

Phase equilibria in the ZrO2–YO1.5–NbO2.5 system at 1300°C and high‐temperature experiments in the ZrO2–YNbO4 subsystem

Phase Transition During Sintering Process Before Nucleation of TFA-MOD YBa2Cu3O7-δ Films

Phase Equilibria in the Fe-Al-Nb(-B) System at 700 °C

PHASE RELATIONSHIPS IN QUASI-SYSTEMS R_2O_3-AlN-Al_2O_3(R=Ce,Pr,Nd,Sm)

Formation Characteristics of the Commensurate Fluorite-Type Bi2O3−Nb2O5 Solid Solution

Synthesis and properties of the NdSF compound, phase diagram of the NdF3–Nd2S3 system

High Pressure-Temperature Study of MgF 2 , CaF 2 , and BaF 2 by Raman Spectroscopy: Phase Transitions and Vibrational Properties of AF 2 Difluorides

Phase Equilibria In The Fe-Nb-Zr Ternary System At 1,200 A Degrees C

Fluorite-pyrochlore-weberite phase transitions in a series of 20-component ultrahigh-entropy compositionally complex ceramics

Isothermal section (500°C) of phase diagram of Nd-Al-Si ternary system

Structural phase transitions in perovskite BaCeO3 with data mining and first-principles theoretical calculations

Phase Diagram of the Quasibinary System LiF–NaF–KF–CeF3

Revisiting Solid-Solid Phase Transitions in Sodium and Potassium Tetrafluoroborate for Thermal Energy Storage

ISOTHERMAL SECTION OF THE ZrO2–HfO2–Eu2O3 SYSTEM PHASE DIAGRAM AT 1100 °C

Competing antiferroelectric and ferroelectric interactions in NaNbO3 : Neutron diffraction and theoretical studies

Phase Equilibria of the System La2O3–NiO–Li2O at 700, 800, and 900°C

Phase equilibria in the Fe–Nb–Zr ternary system at 1,200 °C

Structural Origins of BaF2/Ba1 - Xrxf2 + (x)/rf3 Nanocrystals Formation from Phase Separated Fluoroaluminosilicate Glass: A Molecular Dynamic Simulation Study