Abstract:Creep-fatigue interaction is identified as a primary failure mode for components operating under high temperatures. As operational durations extend, this interaction not only alters the material's microstructures but also initiates a gradual degradation in mechanical properties, significantly impacting its deformation and damage behaviors. In this work, the dynamic microstructural evolution of GH4169 superalloy during creep-fatigue was elucidated via qualitative characterization, and damage level evaluation method was subsequently developed by bridging microstructure degradation to mechanical property degradation. Creep-fatigue tests were performed at 650 °C with various tensile holding times and were interrupted at lifetime fractions of 10 %, 50 % and 80 % for further analysis and tensile evaluations. Results revealed that the prolonged exposure to holding times induced the coarsening of γ″ precipitates alongside an increase in low-angle grain boundaries, culminating a reduction in creep-fatigue strength. The development of voids and cracks exacerbated the degradation of elongation, leading to a hybrid fracture mode encompassing both intergranular and transgranular cracking paths. Synthesizing microstructural evolutions to qualitatively categorize diverse degradation levels imparted a robust physical basis for damage evaluation. A mapping model was established to correlate the average kernel average misorientation (micro-degradation indicator) with the tensile plastic strain energy density (macro-degradation indicator). The damage level evaluation method was endowed with quantitative metrics utilizing this model, and its generality was additionally validated in P92 steel. This work offers an insight into the quantitative damage evaluations of creep-fatigue-induced degradations in materials, thereby providing a theoretical basis for the development of operation management and inspection plans of components.

Investigation of the heat energy and multi‐level load on subsurface fatigue damage evolution via multi‐scale method

An approach to investigating evolution of fatigue damage on surface of structural steel based on microhardness

Research on Fatigue-Creep Interaction Damage of Steel 1.25Cr0.5mo

Determination of relationship between high-temperature low cycle fatigue damage and mechanical property degradation: Experimental and theoretical analyses

Investigation of low cycle fatigue crack propagation behavior of 316H steel at 550°C based on cyclic response and damage accumulation: experiment and modelling

A general energy-based model for fatigue life prediction of high-temperature structural materials

Thermal-mechanical fatigue life prediction considering fatigue-creep interaction effects

A Continuous Low Cycle Fatigue Damage Model and Its Application in Engineering Materials

A New Approach To The Investigation Of Load Interaction Effects And Its Application In Residual Fatigue Life Prediction

A NEW NON-LINEAR CONTINUUM DAMAGE MECHANICS MODEL FOR THE FATIGUE LIFE PREDICTION UNDER VARIABLE LOADING

Strain Energy-Based Fatigue Life Prediction under Variable Amplitude Loadings

Creep-fatigue Damage Level Evaluation Based on the Relationship Between Microstructural Evolution and Mechanical Property Degradation

Multiaxial Fatigue Lifetime Estimation Based on New Equivalent Strain Energy Damage Model under Variable Amplitude Loading

Accumulated crystal plasticity dissipation energy driven continuum damage two-scale model for fretting fatigue initiation life

Experimental Study and Numerical Simulation on High Temperature & Low Cycle Short Fatigue Cracks under Multiaxial Stress States

Life prediction and damage analysis of creep-fatigue combined with high-low cycle loading by using a crystal plasticity-based approach

A Model of Continuum Damage Mechanics for High Cycle Fatigue of Metallic Materials

Experimental investigation and damage modeling of salt rock subjected to fatigue loading

Multi-axial Creep-Fatigue Life Prediction Considering History-Dependent Damage Evolution: A New Numerical Procedure and Experimental Validation

Experimental and Numerical Study of Combined High and Low Cycle Fatigue Performance of Low Alloy Steel and Engineering Application

Thermomechanical fatigue life prediction of metallic materials by a gradient‐enhanced viscoplastic damage approach