Structural confinement-induced highly efficient deep-red emission and negative thermal quenching performance in Mn4+-activated Ca7Mg2Ga6−yAlyO18:Mn4+ phosphors
Jinmei Huang,Pengfei Jiang,Zien Cheng,Rong Wang,Rihong Cong,Tao Yang
DOI: https://doi.org/10.1039/d3qi00252g
IF: 7.779
2023-04-15
Inorganic Chemistry Frontiers
Abstract:High quantum efficiency (QE) and thermally stable emission are indispensable for the application of phosphors. Owing to the strong coupling between the lattice and naked d-orbitals of Mn 4+ , Mn 4+ -activated oxide red-emitting phosphors usually exhibit a low QE and serious thermal quenching (TQ), which strictly inhibit their prospective application. Herein, we rationally designed a novel phosphor series Ca 7 Mg 2 Ga 6− y Al y O 18 :0.02Mn 4+ (CMGA y O:Mn 4+ , 0 ≤ y ≤ 1.5), which adopts a high structural symmetry of the space group F 432. Highly efficient and thermally stable deep-red emissions ( λ em = 721 nm) were achieved simultaneously by structurally confining the Mn 4+ -emitting centres at the isolated octahedrally coordinated sites. Specifically, the highest internal and external quantum efficiencies of 90.2 and 75.9%, respectively, were obtained for CMGA 1.5 O:Mn 4+ due to Al 3+ -alloying-induced local structure modification and suppression of non-radiative transitions. Excellent thermal stabilities of 99, 102.2, and 87.9% of room-temperature photoluminescence intensities were retained at 423 K for CMGA y O:Mn 4+ with y = 0, 0.5, and 1.5, respectively. CMGA 0.5 O:Mn 4+ exhibits an abnormal negative TQ behaviour over the measured temperature range (298–473 K), which is attributed to the energy gain via the electron–phonon interactions of the isolated MnO 6 octahedra. Moreover, in situ high-pressure emission spectra of CMGO:0.02Mn 4+ showed that the emission position is highly sensitive to the external pressure with redshift coefficients of 2.8(2) and 1.16(4) nm GPa −1 in different pressure regions. These excellent photoluminescence properties of CMGA y O:Mn 4+ phosphors signify their great application potential in red LEDs and optical pressure sensors. The findings of this work have paved an avenue for the design of high-performance Mn 4+ -activated phosphors.
chemistry, inorganic & nuclear