Copper Zinc Tin Sulfide Anode Materials for Lithium-Ion Batteries at Low Temperature

Zeru Syum,Tadesse Billo,Amr Sabbah,Boya Venugopal,Sheng-Yu Yu,Fang-Yu Fu,Heng-Liang Wu,Li-Chyong Chen,Kuei-Hsien Chen

DOI: https://doi.org/10.1021/acssuschemeng.1c01341

2021-07-01

Abstract:Developing novel materials is crucial to overcoming the performance degradation of lithium-ion batteries (LIBs) for low-temperature applications. In this work, we demonstrate a novel copper zinc tin sulfide (Cu₂ZnSnS₄, CZTS) thin film with nanowalls structure as the anode material in thin-film LIBs for low-temperature applications. The quaternary CZTS synthesized by a simple hydrothermal method shows a higher reversible capacity of 475 mAh g^–1 after 200 cycles at −10 °C with the EC/DEC/DMC-based electrolyte in comparison with the graphite electrode (110 mAh g^–1 after 100 cycles at −10 °C). The effects of temperature and electrolyte systems including EC/DEC- and EC/DEC/DMC-based electrolytes on the cycling performance are studied. The faster Li-ion transport in the electrolyte–electrode interface of the CZTS anode material is obtained in the EC/DEC/DMC-based electrolyte at −10 °C. In addition, the depth-profiling XPS results of the CZTS anode reveal that a solid electrolyte interphase (SEI) layer with less carbon content is formed in the EC/DEC/DMC-based electrolyte likely associated with the interfacial stability at low temperature. The enhanced cycling performance of CZTS could be attributed to its improved interfacial stability and Li⁺ diffusion, along with the formation of an interconnected active material architecture at low temperature.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acssuschemeng.1c01341?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acssuschemeng.1c01341</a>.Cyclic voltammetry of CZTS with different electrolyte solvents (Figure S1), sulfur K-edge X-ray absorption spectra of CZTS (Figure S2), galvanostatic charge/discharge profile with different electrolyte solvents (Figure S3), charge–discharge profile of MCMB with different electrolytes (Figure S4), ex-situ XRD and Raman analysis of CZTS after 50 cycles at different temperatures and electrolytes (Figure S5), pseudocapacitive contribution in the CV curve obtained with EC/DEC-based electrolyte (Figure S6); O 1s, F 1s, and Li 1s spectra of the CZTS anodes after 50 discharge–charge cycles (Figure S7–S9), discharge capacities of Li-ion batteries at low temperatures (Table S1), and EIS analysis of CZTS (Table S2) (<a class="ext-link" href="/doi/suppl/10.1021/acssuschemeng.1c01341/suppl_file/sc1c01341_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

chemistry, multidisciplinary,engineering, chemical,green & sustainable science & technology