Abstract:Lignin-containing cellulose nanocrystals (LCNCs) were produced from old newspapers using the sulfuric acid hydrolysis process, and the product was used in reinforcing polyvinyl alcohol (PVA) based hydrogel. The lignin content of LCNCs was quantitatively analyzed by X-ray photoelectron spectroscopy (XPS), and LCNCs had 8–19 wt% lignin located on their surfaces. The transmission electron microscopy (TEM) confirmed the presence of lignin on LCNCs as small globular-like particles/patches. The increase in the lignin content of LCNCs increased the thermal stability and hydrophobicity while decreasing the crystallinity of LCNCs. Moreover, the effect of LCNC loading (0.1–1 wt%) on the mechanical strength, rheological properties, swelling behavior, morphology, and thermal stability of PVA-based hydrogel was further elucidated. The incorporation of LCNCs in hydrogel at a low dosage improved the swelling behavior of hydrogel. The lignin present on the surface of LCNCs led to enhanced viscoelasticity, increased compressive strength, and improved thermal stability of hydrogel. In addition, the pore size of the hydrogel dropped more significantly (4.26–1.52 μm) with the use of LCNCs containing more lignin. At a low dosage of 0.1 wt%, all studied properties of hydrogels were improved using the LCNC with high lignin content. This study provides a new prospect for the use of lignin-containing CNCs for the production of a high-performance hydrogel.
What problem does this paper attempt to address?
The problem this paper attempts to address is: improving the mechanical strength, rheological properties, water absorption behavior, morphology, and thermal stability of polyvinyl alcohol (PVA) hydrogels by incorporating lignin-containing cellulose nanocrystals (LCNCs) into the PVA hydrogels. Specifically, the researchers aim to verify the effects of LCNCs with different lignin contents on the performance of PVA hydrogels and explore their potential application in the production of high-performance energy hydrogels.
### Background
- **Limitations of PVA Hydrogels**: PVA is an important synthetic water-soluble polymer that can form chemically or physically cross-linked hydrogels. However, PVA-based hydrogels have low mechanical strength and poor rheological properties, which limit their application range.
- **Attempts to Enhance Materials**: To improve the performance of PVA hydrogels, researchers have tried adding materials such as inorganic clays, metal nanoparticles, and carbon nanotubes. Cellulose nanocrystals (CNCs) are an attractive choice for enhancing PVA hydrogels due to their excellent mechanical properties, large specific surface area, and high tensile strength.
- **Role of Lignin**: Lignin is a natural organic polymer with hydrophobicity and thermal stability. Introducing lignin-containing cellulose nanocrystals (LCNCs) into PVA hydrogels can further improve their performance.
### Research Objectives
- **Preparation of LCNCs with Different Lignin Contents**: Prepare LCNCs with different lignin contents through sulfuric acid hydrolysis.
- **Evaluate the Impact of LCNCs on PVA Hydrogel Performance**: Study the effects of LCNCs with different lignin contents on the mechanical strength, rheological properties, water absorption behavior, morphology, and thermal stability of PVA hydrogels.
- **Explore Application Potential**: Investigate the potential application of LCNCs in the production of high-performance energy hydrogels.
### Main Research Content
- **Preparation and Characterization of LCNCs**: Prepare LCNCs from waste newspapers through sulfuric acid hydrolysis and analyze their surface morphology, chemical composition, and crystallinity using various characterization techniques (such as FE-SEM, TEM, XPS, FTIR, and XRD).
- **Preparation and Testing of PVA Hydrogels**: Incorporate different contents of LCNCs into PVA hydrogels to prepare composite hydrogels and test their mechanical strength, rheological properties, water absorption behavior, morphology, and thermal stability.
- **Results Analysis**: Analyze the specific effects of LCNCs with different lignin contents on the performance of PVA hydrogels based on experimental data.
### Conclusion
- **Role of Lignin**: The presence of lignin improves the thermal stability and hydrophobicity of LCNCs while reducing their crystallinity.
- **Performance Improvement**: The incorporation of LCNCs enhances the water absorption behavior, viscoelasticity, compressive strength, and thermal stability of PVA hydrogels. Particularly, LCNCs with higher lignin content show the most significant improvement in the performance of PVA hydrogels at a low addition level (0.1 wt%).
- **Application Prospects**: This study provides new insights into the use of lignin-containing cellulose nanocrystals for producing high-performance hydrogels, with broad application potential.