Supertough Lignin Hydrogels with Multienergy Dissipative Structures and Ultrahigh Antioxidative Activities
Xiangyu You,Xuelian Wang,Hui Jie Zhang,Kunpeng Cui,Aokai Zhang,Linping Wang,Chandravati Yadav,Xinping Li
DOI: https://doi.org/10.1021/acsami.0c10657
2020-08-12
Abstract:Hydrogels derived from lignin are typically weak and contain only a small amount of lignin, which limits their broad application prospects. In the present work, a novel lignin/poly(<i>N,N</i>-dimethylacrylamide) (PDMA) hydrogel with a high lignin content, superb toughness, and ultrahigh antioxidative performance is constructed by employing a facile dissolve–dry–swell solvent exchange method. Through this process, lignin and PDMA are self-assembled into a multienergy dissipative structure containing rigid lignin-rich domains. Precisely, the PDMA chains both interpenetrated inside and adhered on the surface of these domains through hydrophobic associations. This structure enables the lignin hydrogels to dissipate energy efficiently during the fracture process. At an optimized ultrahigh lignin content of 58% (dry weight basis), the prepared lignin hydrogel exhibited remarkable mechanical properties, such as a high elastic modulus (2.5 MPa), tensile strength (2.5 MPa), and super tensile strain (11.3), and an extremely high fracture energy above 16 000 J m<sup>–2</sup>. In addition, the tough lignin hydrogel exhibited a commendable antioxidant property and nontoxicity. All these advantageous properties provide the lignin/PDMA hydrogels with the potential for use in biomedical materials applications.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c10657?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c10657</a>.Water content and water phase volume of different lignin hydrogels; 1D SAXS profiles [<i>I</i>(<i>Q</i>) as a function of <i>Q</i>] of lignin hydrogels and lignin/PDMA/DMF solutions; 1H NMR spectra of lignin; characterizations of the lignin functional groups; temperature dependence of the storage modulus (<i>G</i>′) and loss modulus (<i>G</i>″) of the pure PDMA hydrogel; tensile curves of the PDMA hydrogels (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c10657/suppl_file/am0c10657_si_001.pdf">PDF</a>)Video of tensile test of DL_8:11 (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c10657/suppl_file/am0c10657_si_002.mp4">MP4</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology