Abstract:Deep drawing is the most advanced sheet metal forming technique. In today’s demanding environment is the global environment and energy saving, the process has been supposed to play a vital role in light-weight component industry. Light-weight, high strength, low density and extreme corrosion aspects must be almost guaranteed in a deep drawn product. However, due to those requirements, thinning and wrinkling and other defects will be increased also. Numerous elements such as blank-holder pressure, punch force, speed of punch, blank shape, thickness variation, surface-to-surface friction coefficient, material characteristic,...influenced to the success of methods as well as the quality of the products. In addition, worldwide manufacturers keep getting the most goods done in less time. Indeed, the increasing of productivity should be also dealt because it proportionally relates to the stamping speed. This paper investigates the influence of punch velocity on deformation behavior of aluminum alloy 5052–H112. Finite Element Method was used to perform Nakajima test at several of punch velocities of specimen widths and monitor fluctuations in magnitude of von Mises stress, the major strain and minor strain. Forming Limit Curve (FLC) was obtained at different velocities and almost uniform. Stretching and sliding across the top of the punch resulted in thinning of sheet metal. Beside this, the action of punch stroke resulted in the production of more von Mises concentrated stress and the largest specimen in widths had shown the peak value of von Mises stress compared with the other specimens at all different velocities. Furthermore, the ratio of the major strain to the minor strain is influenced by the mass of material at the contact area and keeps consistent over the variation in velocities of punch. This will pave the way for future studies of the optimization of the stamping speed in deep drawing.

Deformation and fracture behavior of 5052 aluminum alloy by electromagnetic-driven stamping

Fracture behavior of 7075-T6 aluminum alloy under electromagnetic forming and traditional stamping

Study on Simulation of Stamping Forming and Die Surface Optimization of Aluminum Alloy Plate

Deformation behavior and mechanical properties of 5052-O aluminum alloy joints formed by high-speed clinching

Deformation Mechanism of 5052 Aluminum Alloy Using Electrically Assisted Electromagnetic Forming

Forming Limit and Mechanical Properties of 2024-O Aluminum Alloy Under Electromagnetic Forming

Enhance forming properties of 7075-T6 aluminium alloy by two-step electromagnetic forming and electrical pulse treatment

Improved forming capability of 7075 aluminum alloy using electrically assisted electromagnetic forming

Microstructure evolution of aluminum alloy under quasi-static, mechanical dynamic, and electromagnetic dynamic deformation

Deformation Behavior and Properties of 7075 Aluminum Alloy under Electromagnetic Hot Forming

Microstructure and mechanical properties of AA5052 after electromagnetic hydraulic forming

Manufacture of complex shape parts by high-speed electromagnetic hydraulic forming method

Analysis of the Stamping Speed for Sheet Metal Forming of Aluminum Alloy 5052-H112

Effect of initial state on formability of AA1060 alloy under quasi-static and electromagnetic forming

Deformation behavior and formability of solid solution state Al–Li alloy in electromagnetic forming

Electromagnetic driven forming utilizing a metal ring for controlling shapes of sheet metals

Large ellipsoid parts manufacture using electromagnetic incremental forming with variable blankholder structure

Improving formability of AZ31B magnesium alloy induced by twinning multiplication and annihilation during electromagnetic forming

Dynamic Analysis of Closed Die Electromagnetic Sheet Metal Forming to Predict Deformation and Failure of AA6061-T6 Alloy Using a Fully Coupled Finite Element Model

Damage and failure characterization of 7075 aluminum alloy hot stamping

AA5052 failure prediction of electromagnetic flanging process using a combined fracture model