Abstract:Large ellipsoid parts are prone to wrinkle when forming by using traditional stamping. Aiming to solve the wrinkling problem in large parts, the EMIF method with a variable blank holder is proposed in this paper. The numerical simulation has shown that the sheet material near the blank holder is, as a consequence of stamping, subjected to circumferential compressive stress. When the drawing height was 100 mm, the sheet metal was notably wrinkled. In the electromagnetic forming (EMF) process, the sheet region facing the coil becomes thinner. However, the sheet metal thickness corresponding to the coil edge increases with the increase in forming height. If the EMF forming height is 150 mm, the sheet, which is in contact with the smooth mold, is deformed without a wrinkle. Compared to traditional stamping, the EMF can significantly reduce the sheet metal wrinkling, improving the deformation height of the sheet metal smooth area.
What problem does this paper attempt to address?
This paper attempts to solve the wrinkling problem that occurs during the manufacturing of large ellipsoidal parts. Specifically, the traditional stamping forming method is prone to cause material wrinkling when manufacturing large parts, especially when the ratio of material thickness to diameter is approximately 0.1%, and this phenomenon is particularly severe. To solve this problem, the author proposes a method that combines electromagnetic incremental forming (EMIF) and a variable blank - holder structure. Through this method, material wrinkling can be significantly reduced, and the deformation height of the smooth area of the formed part can be increased, thereby improving the manufacturing quality of large ellipsoidal parts.
### Background of the Paper
With the increasing demand for integral, high - precision, and lightweight structural parts in high - speed trains, large - scale airplanes, and large - scale launch vehicles, the development of thin - plate parts has been rapid. These applications require the production of parts with larger sizes, thinner walls, deeper cavities, and more complex surfaces, while using materials that are difficult to deform. For example, aluminum alloy has been widely used in the aerospace field due to its low density, high strength, and corrosion resistance.
### Problem Description
Large ellipsoidal parts are key components of rocket storage tanks, and their required shapes are mainly achieved by applying mechanical forces and liquid pressures to drive part deformation. Currently, there are two main methods for manufacturing large - scale rocket storage tanks:
1. Decompose the part into small parts and weld them together after forming.
2. Use heavy - duty equipment to achieve the integral manufacturing of large - scale parts.
However, both of these methods have some problems:
- The decomposition and welding method requires multiple mold tests, which increases the mold manufacturing cost and is inefficient.
- Although the method using heavy - duty equipment can achieve integral manufacturing, the equipment is bulky, expensive, and poses a great challenge to the equipment manufacturing industry.
### Solution
To solve the above - mentioned problems, especially the problem of material wrinkling in the traditional stamping process, the author proposes a method that combines electromagnetic incremental forming (EMIF) and a variable blank - holder structure. Through numerical simulation and experiments, the forming process and wrinkling phenomenon were studied, and the results show that:
- In the traditional stamping process, when the drawing height reaches 100 mm, the material wrinkles obviously.
- In the electromagnetic forming (EMF) process, the material close to the coil becomes thinner, while the material thickness corresponding to the edge of the coil increases with the increase of the forming height. When the EMF forming height is 150 mm, the material in contact with the smooth mold does not wrinkle.
### Principle of the Method
The process of electromagnetic incremental forming (EMIF) includes two steps:
1. Use the initial blank - holder radius \( R_1 \), and gradually form to the final forming depth \( H_1 \).
2. Change the blank - holder radius to \( R_2 \), and continue to gradually form to the final forming depth \( H_2 \).
Through this method, material wrinkling can be effectively reduced without increasing the complexity of the equipment, and the quality and performance of the formed part can be improved.