Ion-exchanged LTA zeolite derived nepheline phase NaAlSiO4:Eu2+ ceramic phosphor for laser illumination

Yuxiao Fan,Hui Lin,Hongwei Liu,Linjing Zhang,Jiaying Wang,Qi Xie,Li Zhou,Ruijin Hong,Dawei Zhang,Yanna Tian,Jie Chen,Shengming Zhou

DOI: https://doi.org/10.1016/j.ceramint.2021.07.229

IF: 5.532

2021-11-01

Ceramics International

Abstract:A reliable yellow phosphor converter that can be efficiently excited by a 405 nm bluish violet laser is in high demand for laser illumination applications. A NaAlSiO4:Eu2+ phosphor with a quantum efficiency reaching 92% was obtained using LTA zeolite as the raw material. NaAlSiO4:Eu2+ ceramics with suitable porosities for laser illumination were prepared from the phosphor powders via spark plasma sintering. The ceramics lost only 2% of the quantum efficiency compared to the powders, maintained good thermal quenching properties (30% drop at 150 °C), and showed good thermal conductivity (2.02 W‧m−1‧K−1). The NaAlSiO4:Eu2+ ceramic with 405 nm bluish violet lasers, with the increase in laser power density to 9.15 W/mm2, exhibited an increasing luminous flux (23.83–70.26 lm) and maintained a stable luminous efficacy (47.7–46.8 lm/W), and the temperature distribution of the ceramic remained uniform and stable under long-time laser irradiation. This indicates that the nepheline-phase NaAlSiO4:Eu2+ ceramic is a promising material for laser illumination.

materials science, ceramics