Microstructure and mechanical properties of 3D printed ceramics with different vinyl acetate contents

He Li,Yong-Sheng Liu,Yan-Song Liu,Qing-Feng Zeng,Jing-Jing Liang
DOI: https://doi.org/10.1007/s12598-020-01685-x
IF: 6.318
2021-03-02
Rare Metals
Abstract:<span class="a-plus-plus abstract-section id-a-sec1"><p class="a-plus-plus">Stereolithography (SL)-based three-dimensional (3D) printing technique is an efficient method for the fabrication of alumina ceramics. The alumina slurry is difficult to obtain due to the barrier between hydrophilic alumina and oleophilic resin. It not only requires that the ceramic slurry possessed low viscosity and uniformity, but also requires that the slurry could complete the photocuring process. In this study, vinyl acetate was added in the ceramic slurry as a bridge to connect alumina and resin, and the effects of vinyl acetate content on the microstructure and mechanical properties of the alumina ceramics were systematically investigated. The results showed that the alumina ceramics were composed of three types of particles which included large aggregates, individual particles, and long-column-shaped particles. The shrinkage, bulk density, and crystallite size of the ceramics increased with the increase in vinyl acetate content. The open porosity decreased with the increase in vinyl acetate content. The flexural strength of the ceramics first increased and subsequently decreased with the increase in vinyl acetate content. The shrinkage in <em class="a-plus-plus">Z</em> direction was much greater than that in <em class="a-plus-plus">X</em> or <em class="a-plus-plus">Y</em> direction. Based on the above results, the optimum vinyl acetate content for alumina slurry was 10 wt%, which resulted in sintered ceramic with the shrinkage of 15.6% in <em class="a-plus-plus">X</em> direction, 13.5% in <em class="a-plus-plus">Y</em> direction, 21.9% in <em class="a-plus-plus">Z</em> direction, bulk density of 1.9 g·cm<sup class="a-plus-plus">−3</sup>, open porosity of 50.1%, and flexural strength of 24.4 MPa. The sintered ceramics satisfy the requirement of alumina ceramic cores.</p></span><span class="a-plus-plus abstract-section id-a-sec2 outputmedium-online"><h3 class="a-plus-plus">Graphic abstract</h3></span>
materials science, multidisciplinary,metallurgy & metallurgical engineering
What problem does this paper attempt to address?
The paper primarily explores the microstructure and mechanical properties of 3D-printed alumina ceramics with varying vinyl acetate content, produced using stereolithography (SL) technology. The core issue addressed in the paper is the challenge in the preparation process of alumina slurry, specifically the barrier problem between hydrophilic alumina and hydrophobic resin. The authors propose adding vinyl acetate to the slurry as a bridge to improve the bonding strength between alumina powder and resin. They also investigate the effect of varying vinyl acetate content on the final ceramic's microstructure and mechanical properties. Specifically, the study found that: 1. With the increase in vinyl acetate content, the shrinkage rate, bulk density, and grain size of the alumina ceramics all increased, while the porosity decreased. 2. The flexural strength of the alumina ceramics first increased and then decreased with the increase in vinyl acetate content, reaching a maximum value of 24.4 MPa at 10wt% vinyl acetate content. 3. The shrinkage rates in the X, Y, and Z directions were different, with the shrinkage rate in the Z direction being significantly greater than in the X and Y directions. 4. The optimal vinyl acetate content was 10wt%, at which the sintered ceramics exhibited better performance, including shrinkage rate, bulk density, porosity, and flexural strength. In summary, the paper aims to improve the performance of 3D-printed alumina ceramics by optimizing the amount of vinyl acetate added, to meet specific application requirements, such as for manufacturing ceramic cores for hollow blades in aircraft engines.