Abstract:<p>In this research, three new Schiff bases were synthesized by paeonol and amino acids and tested as corrosion inhibitors for Mg-Zn-Y-Nd alloy. Weight loss measurements and electrochemical measurements demonstrated that three Schiff bases showed high inhibition efficiency on Mg corrosion. The corrosion products on Mg surface were analyzed by scanning electron microscopy (SEM), Fourier transform infrared spectrum (FTIR) and X-ray photoelectron spectroscopy (XPS). The possible inhibition mechanism was proposed, in which the Schiff bases react with Mg<sup>2+</sup> ions to form complexes on Mg surface in inhibitors-containing electrolytes. The theoretical calculation of quantum chemical demonstrated the experimental findings.</p>
What problem does this paper attempt to address?
The paper mainly discusses the corrosion inhibition of Mg-Zn-Y-Nd alloy in normal saline solution. Three new Schiff bases were synthesized in the study and used as corrosion inhibitors to reduce the corrosion of magnesium alloy. Through weight loss measurements and electrochemical measurements, it was found that these three Schiff bases exhibited high inhibitory efficiency against magnesium corrosion. Experimental analysis suggested that the Schiff bases may react with Mg2+ ions to form complexes on the magnesium surface, thereby preventing magnesium dissolution. Theoretical quantum chemical calculations confirmed the experimental results.
The paper also mentions the importance of magnesium alloys in various applications due to their low density, high strength, recyclability, and biodegradability. However, their high chemical activity and fast corrosion rate lead to early failure. Corrosion inhibitors can reduce the corrosion rate of metal materials without altering their physical and mechanical properties. Organic corrosion inhibitors such as Schiff bases have received attention due to their ability to form protective layers on the magnesium surface. However, for biomedical magnesium alloys, efficient, non-toxic, and degradable corrosion inhibitors are required, which is currently a key research focus.
The experimental section includes the synthesis of Schiff bases, immersion tests, electrochemical measurements, surface analysis, etc., to evaluate the effectiveness and action mechanism of the inhibitors. Through immersion tests and electrochemical tests (such as open circuit potential, polarization curves, and impedance spectra), the authors found that these Schiff bases can effectively inhibit the corrosion of magnesium alloys, and the morphology and composition of corrosion products were analyzed by SEM, FTIR, and XPS. The theoretical calculations support the observed inhibition effects in the experiments.
In summary, the paper aims to develop and validate efficient, non-toxic, and degradable corrosion inhibitors for biomedical magnesium alloys to improve their durability and safety in corrosive environments.