Achieving an appropriate strength-ductility synergy of Nbss/Nb5Si3 in situ composites governed by gradient annealing heat treatment

Yu Wang,Lina Jia,Chengtong Ye,Hu Zhang

DOI: https://doi.org/10.1016/j.matchar.2022.112312

IF: 4.537

2022-11-01

Materials Characterization

Abstract:The time-temperature gradient annealing heat treatment (TTGA) was performed on the directionally solidified Nb-16Si-23Ti-4Cr-2Al-2Hf-0.4Re (at.%) alloy to investigate the microstructure morphology, precipitated behaviors, room temperature mechanical properties and damage evolution. The Nbss, αNb5Si3 and γNb5Si3 are all the ever-present constituent phases throughout the whole annealing process. After gradient annealing at 850 °C for 12 h, the TTGA induces another four precipitating behaviors: (i) bulk fcc-Ti precipitates along Nbss/αNb5Si3 interface; (ii) fcc-Ti partially transforms into hcpTi; (iii) ultrafine fcc-Ti disperses inside Nbss; (iv) spherical γNb5Si3 precipitates from internal of Nbss. For conventional heat treatment, the room temperature fracture toughness and ultimate tensile strength of CHT alloy are 13.1 MPa·m1/2 and 1046.7 MPa respectively. After TTGA at 850 °C for 12 h, the KQ in GA-1 alloy increases to 21.6 MPa·m1/2 with higher of 64.9%. Owing to higher continuity and better deformability of Nbss matrix, more toughening mechanisms as crack bifurcation, deflection and bridging, especially microcrack and Nbss/αNb5Si3 interface decohesion can be observed in GA-1 alloy. In addition to achieve roughly the equivalent UTS (1012.3 MPa) compared with other gradient annealed alloys, GA-1 alloy also exhibits obvious tensile plasticity.

materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing