Dependence of ductile-brittle transition related with serrated flow on viscosity dominated by glass forming ability in ZrxTi65-xBe27.5Cu7.5 metallic glasses

Xiangkui Liu,Tianchi Wang,Xinxiang Song,Zibo Zhang,Qipeng Wang,Shuai Feng,Yang Yang,Jian Kong

DOI: https://doi.org/10.1016/j.msea.2021.141057

2021-04-01

Abstract:The transition in deformation mode from ductile to brittle related with glass forming ability (GFA) was systematically investigated via uniaxial compression tests in ZrxTi65-xBe27.5Cu7.5 metallic glasses (MGs). As the GFA increases, both the number and amplitude of serrated flow decrease gradually in stress-strain curves. There are two main reasons for the reduction in viscosity during shear deformation. First, the larger elastic energy is mainly dissipated in the form of heat and the temperature rises within shear bands beyond the melting points. Second, the MGs with better GFA contain larger excess quenched-in free volume due to rapid solidification. Based on the Cohen-Grest model, large free volume can effectively decrease the atomic packing density and reinforce the mobility of atoms, greatly reducing the viscosity during shear deformation. Hence, for the reduction of the viscosity during deformation, the coupling effect of temperature and free volume matters. Multiple shear bands are activated by applied stress and interact strongly with each other, significantly improving the plasticity. The initiation of multiple shear bands is an indicative of much serrated events in stress-strain curves. Thus, the change in viscosity associated with GFA dominates the occurrence of serrated flow, facilitating the transition between ductile and brittle deformation.

materials science, multidisciplinary,nanoscience & nanotechnology,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

This paper aims to explore the plastic - brittle transition mechanism related to glass - forming ability (GFA), especially in ZrxTi65 - xBe27.5Cu7.5 metallic glasses. Through uniaxial compression tests, the influence of different Zr contents on the serrated flow behavior of these metallic glasses during the deformation process was studied. As the GFA increases, the number and amplitude of serrated flows in the stress - strain curves gradually decrease. This is mainly attributed to two reasons: First, the elastic energy within the shear band is mainly dissipated in the form of heat, causing the temperature to rise above the melting point; second, metallic glasses with better GFA contain more quenching residual free volume due to rapid solidification. Based on the Cohen - Grest model, a large free volume can effectively reduce the atomic packing density, enhance atomic mobility, and thus significantly reduce the viscosity during shear deformation. Therefore, the reduction in viscosity is closely related to GFA, which dominates the occurrence of serrated flow and promotes the transition from plastic to brittle deformation.