Microstructural and Mechanical Properties Analysis of Phosphate Layers Deposited on Steel Rebars for Civil Constructions

Petru Lazar,Nicanor Cimpoesu,Bogdan Istrate,Alin Marian Cazac,Diana-Petronela Burduhos-Nergis,Marcelin Benchea,Andrei-Constantin Berbecaru,Gheorghe Badarau,Gabriel Dragos Vasilescu,Mihai Popa,Costica Bejinariu

DOI: https://doi.org/10.3390/coatings14020182

IF: 3.236

2024-02-01

Coatings

Abstract:This paper carries out a study on the microstructural characteristics and mechanical properties of phosphate layers deposited on steel reinforcements for civil constructions. Analyses were performed on 4 sets of samples: 1 control sample (unphosphated) and 2–4 samples that were phosphated with three different solutions. The structural and chemical analysis, as well as the examination of the mechanical properties (surface roughness, microindentation, and scratch resistance) of the phosphate layers deposited on steel rebars for civil constructions, was carried out. The following conclusions were drawn from the experimental results: the coatings show flashes of crystals deposited on the metal surface; chemical homogenization of the phosphated layers is observed; the profiles present a higher roughness after deposition of the phosphated layers; the indentation Young modulus and hardness values recommend the phosphating procedure to improve the CS surface quality; the COF is three times larger for phosphated samples compared with the initial metallic one; and scratch traces are uninterrupted, except for one zone of sample that was phosphated with solution II, wherein the phosphated layer does not present lateral scratches or exfoliations.

materials science, multidisciplinary,physics, applied, coatings & films

What problem does this paper attempt to address?

The paper aims to study the microstructural characteristics and mechanical properties of the phosphating layer on rebar to improve the corrosion resistance and bonding performance with concrete in construction engineering. Specifically, the paper explores the effects of different phosphating solutions on the rebar surface through the following experimental methods:

1. **Experimental Design**:
- Four samples were used: one unphosphated control sample and three samples treated with different phosphating solutions.
- The structure, chemical composition, and mechanical properties (such as surface roughness, microhardness, and scratch resistance) of the phosphating layer were studied.

2. **Materials and Methods**:
- The experiment used CS37 carbon steel (10 mm in diameter), which is a smooth and hot-rolled concrete rebar.
- The phosphating layer was deposited on the sample surface through a chemical conversion process (phosphating), using three phosphating solutions with different chemical compositions.

3. **Results and Discussion**:
- The results showed that the phosphating layer surface was covered with deposits of compounds from the electrolyte solution, and there were some intergranular regions, leading to a relatively rough surface.
- The surface roughness increased after phosphating, which is beneficial for improving the bonding performance between the rebar and concrete.
- After treatment with different phosphating solutions, the surface roughness parameters (such as Ra values) changed significantly, indicating that the phosphating layer can affect the friction coefficient, microhardness, and wear resistance.

In summary, this study aims to optimize the application of rebar in construction by analyzing the microstructure and mechanical properties of the phosphating layer, particularly enhancing its corrosion resistance and bonding strength with concrete.