Abstract:Titanium alloys are known for being difficult to machine. Within the groups of Ti alloys, the machinability is reduced when going from the α-alloys, to α + β, and finally to near-β or β-alloys. Uncoated cemented carbide is traditionally used for machining these alloys and finding a suitable coating to improve the performance is a challenge due to the high strength of Ti alloys and the high chemical reactivity of Ti with tool and coating materials at the temperatures achieved during cutting. The PVD applied Ti x Al 1-x N (x = 0.4–0.7) is generally recommended for machining Ti alloys and a top layer of NbN has shown promising performance in milling applications. This study systematically explores the wear mechanisms of either uncoated WC-12%Co or its Ti 0.45 Al 0.55 N-NbN coated version in the milling of Ti alloys ranging from near-α (Ti-6Al-2Sn-4Zr-2Mo), α + β (Ti-6Al-2Sn-4Zr-6Mo), and near-β (Ti-5Al-5Mo-5 V-3Cr) alloys. The wear evolution is explored by studying as-worn tools and their cross-section using SEM-XEDS and EBSD after having reached 10%, 30%, 50%, and 100% of the full tool life at a flank wear criterion VB = 200 μm. The coating is removed within seconds of engagement and fails by cracking within the bulk and PVD droplet defects can initiate such cracks. Diffusional dissolution of the coating may be active on a minor scale, but the rapid mechanical failure shows the need for a more robust coating formulation. Exposed cemented carbide is worn at varying intensities when machining the Ti alloys. The highest wear rate is achieved in milling α + β Ti-6246, followed by a moderate wear rate in near-β Ti-5553, and with a slower wear rate in milling near-α Ti-6242 which is explained varying intensities in oxidation wear, diffusional dissolution, and mechanical cracking. Diffusional loss of C gives rounder WC grains and remaining W at the interface is removed by the chip flow. Diffusional loss of Co gives reduced grain bonding and loss of the dampening effect that leads to fractures in WC grains. Specifically in milling α + β Ti-6246 and in minor scale in near-α Ti-6242, there is formation of CoWO 4 ceramic present several μm into the tool and its formation is facilitated by the oxidation of binder with resolved W. Fractures within the CoWO 4 explains the high wear rate. Cracks also propagate in binder regions initiated from weakened interface regions due to diffusional loss of C and Co.

Influence of V concentration in TiAlSiVN coating on self-lubrication, friction and tool wear during two-pass dry turning of austenitic steel 316 L

Comparative analysis over microstructural, mechanical properties and cutting performance of TiN, TiVN coatings deposited by magnetron sputtering on SiAlON ceramic tool insert

An Investigation of the Effect of Novel Mono/Bi-Layered PVD-Coated WC Tools on the Machinability of Ti-5Al-5V-5Mo-3Cr

Insights into the oxidation resistance mechanism and tribological behaviors of multilayered TiSiN/CrVxN hard coatings

Tribological behaviour of TiAlN and AlCrN coatings on stainless steel

Cutting Performance of TiN/TiSiN Coated Tool during Turning of Ti6Al4V Titanium Alloy

Tool surface modification methodology to improve the machinability of Ti6Al4V through combination of micro-EDM texturing and AlSi-10Mg soft coating techniques in dry turning

Optimizing machining efficiency: a comprehensive study on PVD cathodic arc evaporation coated turning tool inserts with TiAlN/AlCrN multilayer coatings

Machinability Performance of Single Coated and Multicoated Carbide Tools During Turning Ti6Al4V Alloy

Wear Behavior of TiAlVN-Coated Tools in Milling Operations of INCONEL® 718

Tribological properties of in-situ PVD TiAlN, TiSiN, and TiAlN/TiSiN coatings under ambient air and vacuum environment

Properties and Performance of TiAlSiN and AlCrN Monolayer and Multilayer Coatings for Turning Ti-6Al-4V

Wear Behavior and Machining Performance of TiAlSiN-Coated Tools Obtained by dc MS and HiPIMS: A Comparative Study

Enhancing Tool Performance in High-Speed End Milling of Ti-6Al-4V Alloy: The Role of AlCrN PVD Coatings and Resistance to Chipping Wear

Effects of V and Cu codoping on the tribological properties and oxidation behavior of AlTiN coatings

Effects of PVD CrAlN/(CrAlB)N/CrAlN Coating on Pin–Disc Friction Properties of Ti2AlNb Alloys Compared to WC/Co Carbide at Evaluated Temperatures

Tribological Aspects of Cutting Tool Wear during the Turning of Stainless Steels

On wear of TiAlN coated tools with and without NbN overlayer in machining titanium alloys

On the wear mechanisms of uncoated and coated carbide tools in milling titanium alloys

Experimental investigation of uncoated, single layer, and multilayer-coated TiAlN/TiN tool inserts in dry orthogonal cutting of AISI/SAE 4140 alloy steel

Sliding friction and wear behaviour of ion nitrided and TiN coated AISI 4140 steel