Abstract:Lithium-sulfur batteries (Li-S batteries) with high energy density and low cost are promising next-generation energy-storage devices. The commercialization of Li-S battery is hindered by poor cycling efficiency. Herein, SiO2 nanotubes (SNTs) were prepared through the template method with ammonium DL-tartrate template. And multifunctional interlayer (SNTs@CP) composed of the SNTs and the carbon nanotube paper (CP) was fabricated to suppress the polysulfide shuttle effect in Li-S batteries. The SNTs@CP interlayer could efficiently absorb polysulfides (LiPSs) through the polarization sites of SiO2. Moreover, conductive network can be formed by CP to enhance the rate capability and cycling performance. And the mesoporous hollow structure of the SNTs can facilitate the diffusion of Li ions. Results show that Li-S batteries with the SNTs@CP interlayer retain high specific capacity of 911 mA h/g after 80 cycles at 0.5 C, with the coulombic efficiency of 98%. Our work provides a promising new strategy to build high energy density Li-S battery.

High-performance lithium-sulfur batteries achieved by a multifunctional SiO2-nanotubes/carbon composite interlayer