Abstract:Additive manufacturing (AM) of biomedical materials provides enormous opportunities to fabricate multifunctional and structurally designed frameworks for tissue engineering, such as dental implants and bone substitutes. Despite several advantages of the binder jet 3D printing technology over other AM methods, for example, no limitations in materials selection, high materials recycling efficiency, no thermal stress development, no need to support materials, and the possibility of fabrication of printing functionally graded materials, the fabrication of biomedical-grade titanium alloys with high-density, fine microstructure, and low pickup of impurities is still challenging. This work presents the effects of powder particle size and 3D printing conditions on the microstructural features and mechanical properties of Ti-6Al-4V alloy. The formation of large and inter-aggregate pores during binder jetting is demonstrated and discussed. Design and selection of particle size distribution with a mean diameter of ~20 μm and large span and positive skewness are proposed to minimize binder-induced powder aggregation and fabricate green parts with a density of 65±1% PFD (pore-free density). Dilatometric studies under a partial pressure of argon (0.1 bar) determine that sintering just above the α/β transus temperature (~980 °C) provides a high strain rate to remove pores, but high-temperature sintering (≥1250 °C) is required to attain 97% PFD. The successful fabrication of high-density Ti-6Al-4V parts (≥96% PFD) with the microstructure comparable to metal injection molding (MIM) titanium parts (≈100 μm α grains + β lattes) is demonstrated. The tensile strength and elongation values fall in the range of 880±50 MPa and 6±2% (depending on the processing condition), which is comparable with metal injection molded parts and superior to the laser powder bed fusion technology concerning ductility. The content of carbon (<0.02 wt.%) and nitrogen (0.01 wt.%) also falls in the standard region of metal injection molding. However, oxygen pickup during sintering moderately increases the oxygen content (for 30–50%) over the standard level. The concentration of interstitials entrapped in the metal is comparable to that of parts manufactured by the powder bed fusion process, but the mechanical properties are better matched with the commercial titanium alloy. The fabrication of the titanium alloy as per the ASTM F2885 standard provides an excellent opportunity for the binder jetting process to develop custom-made biomaterials.

Direct ink writing of porous Ti6Al4V alloys via UV light curing

Direct ink writing of metal parts with curing by UV light irradiation

Preparation and mechanical performance analysis of porous Ti6Al4V scaffold fabricated by direct ink writing

Preparation, Characterization and Designing of Porous Ti–6Al–4V Through Metal Injection Molding Without Space Holder

Densification, Tailored Microstructure, and Mechanical Properties of Selective Laser Melted Ti–6Al–4V Alloy via Annealing Heat Treatment

Microstructural development during additive manufacturing of biomedical grade Ti-6Al-4V alloy by three-dimensional binder jetting: material aspects and mechanical properties

Investigating mechanical and surface porosity values of high-performing 3D-printed titanium alloys along with stress-relieving heat treatments

Effect of Heat Treatment on Microstructure and Mechanical Properties of Ti6Al4V Alloy Fabricated by Selective Laser Melting

Fabrication of Ti3Al-Based Intermetallic Alloy by Laser Powder Bed Fusion Using a Powder Mixture

Effect of Laser Sintering Parameters on the Microstructure, Mechanical Properties and Corrosion Behavior of Titanium Grade 5 Alloy

Three-dimensional porous tungsten via DLP 3D printing from transparent ink

Direct 3D Printing of Low Melting Point Alloy Via Adhesion Mechanism

Binder Jetting 3D Printing of Titanium Aluminides Based Materials: A Feasibility Study

Microstructure and compression properties of 3D powder printed Ti-6Al-4V scaffolds with designed porosity: Experimental and computational analysis

Microdeformation and strengthening mechanism of 3D printed TC4/TC11 gradient titanium alloy subjected to tensile loading

Tailoring mechanical properties of FDM-3D-printed parts through titanium dioxide-reinforced resin filling technique

Microstructure and Electrochemical Behavior of a 3D-Printed Ti-6Al-4V Alloy

Direct Write Printing of Three-dimensional Photocatalytic TiO2 Structures

In situ design of advanced titanium alloy with concentration modulations by additive manufacturing

Additive Manufacturing of Ultrafine-Grained High-Strength Titanium Alloys

Microstructure Tailoring for High Strength Ti-6Al-4V without Alloying Elements through Optimized Preheating and Post-Heating Laser Scanning in Laser Powder Bed Fusion