Ion Doped Lead-Free Double Perovskite Cs2NaBiCl6 with Multiple Excitation and Tunable Emission towards Light Emitting and Anti-counterfeiting Applications
Junxiang Pei,Haofeng Li,Xiaodong Yuan,An Su,Dechao Yu,Dawei Zhang
DOI: https://doi.org/10.1039/d4tc03715d
IF: 6.4
2024-10-20
Journal of Materials Chemistry C
Abstract:Lead-free double perovskite has been emerging as an intriguing optical material particularly due to its non-toxicity, higher instability, and tunable multicolor luminescence. Herein, Cs2NaBiCl6 (CNBC) double perovskite was employed as a versatile host to accommodate ionic dopants for multicolor emission properties. By Br- ion doping, excitation peak can be modulated continuously from 357 to 374 nm, which, such as the CNBC:30%Br- sample, just cover the emitting light of commercial ultraviolet (UV) ~ 365 nm chip for possible lighting application. Moreover, doping of Mn2+ into CNBC:30%Br- will retain the UV ~ 365 nm excitation characteristics but with much strengthened intensity. The CNBC:30%Br-, Mn2+ yields robust broadband emission at 585 nm from the 4T1 (4G) → 6A1 (6S) transition of Mn2+, which after optimizing Mn2+ concentration (about 15%) is about 72 times stronger than the emission of CNBC upon 365 nm excitation. Energy transfer from the self-trapping excitons (STE) state of halogen double perovskite to Mn2+ activator, as well as the concentration quenching of Mn2+, were rationally proposed on basis of experiments and theories. Using our prepared CNBC:30%Br-,15%Mn2+ phosphor, a white light-emitting diode (WLED) with CIE chromaticity coordinate (0.35, 0.33) was fabricated with mixing commercial BaMgAl10O17: Eu phosphors on a UV ~ 365 nm chip. Most interestingly, the CNBC:30%Br-,15%Mn2+ can further host Er3+ and Yb3+ ions for a novel material that can be excited by 365 nm for orange luminescence and by 980 nm for unique green up-conversion, respectively. With help of screen printing, information encryption/decryption and optical anti-counterfeiting were practically carried out under irradiation of 365 and 980 nm, which can be further developed into a promising multi-level fluorescent anti-counterfeiting technology using these lead-free double perovskite systems.
materials science, multidisciplinary,physics, applied