Abstract:Accurate prediction of fatigue performance and life is a key issue in the design and applications of the high strength-to-weight ratio of many contemporary magnesium alloys, which are suitable for ultimate weight reduction purposes in automotive and aircraft components. For example, the ever increasing demands for higher efficiency and light weight typical cases of power generation, aerospace and automotive industries call the maximum exploitation of the material’s properties. The combination of low density (about 1.74 g/ cm3), high specific strength and excellent castability qualifies magnesium alloys as ideal materials for the lightweight constructions [1]. Thus, purely empirical models that heavily rely on larger safety factors are of limited uses. It is now widely recognized that fatigue damage models that are closely related to the microstructural features to provide a more reliable basis for a life prediction, provided that the relevant microstructural damage mechanisms are accurately accounted for. Therefore, there are increasing interests in the fatigue tests combined with the high-resolution microscopic techniques, environmental influencing factors, and especially in understanding their fatigue crack initiation and propagation behaviors with process rationalization [2-4]. Subsequently experimental observations on cast magnesium alloys have accumulatively revealed that the dendrite cell size, pores, secondary phase particles, persistent slip bands and twinning in the dendrite cells considerably affect on the fatigue durability and fatigue cracking behavior or crack growth mechanism of dendritic magnesium alloys [5-8]. The quantitative estimation of small fatigue crack growth rate of cast magnesium alloys is whether simply and effectively to assist the reversed design of cast magnesium alloys or ceaselessly to improve the strength and toughness of cast magnesium alloys. At the same time, it is necessary how to understand that these microstructural features of cast magnesium alloys play role in the fatigue cracking behavior or that the microstructural evolution reacts to the applied loadings. However, it is difficult to use conventional alloying techniques to improve some of their properties, e.g. elastic modulus, elastic-plastic deforming property and the different thermal expansion between phases during the shrinking at the high elevated temperatures. Under these conditions the elastic, and the possible plastic, properties of the secondary phase will influence the mechanical response during an applied loading since the interface of secondary phase will transmit stresses from the matrix around the secondary phase when the interface both the matrix and secondary phase has a compatible strain field. If the elastic

Effect of Shrinkage Versus Hydrogen Pores on Fatigue Life of Cast AlSi11Mg Alloy

Effects of Crack Position on Fatigue Life of Large Seamless Storage Vessels Made of 4130X for Hydrogen Refueling Station

Preliminary Study on Simulation of Microporosity Evolution and Fatigue Life of Aluminum Alloy Casting

Design Fatigue Life Evaluation of High-Pressure Hydrogen Storage Vessels Based on Fracture Mechanics

Failure Behavior of High Pressure Die Casting AZ91D Magnesium Alloy

Casting Aluminum Fatigue Assessment Correction Method Based on Crack Propagation Prediction

Fracture Behavior of a High Pressure Die Casting AlSi10MnMg Alloy with Varied Porosity Levels

Hydrogen microporosity evolution and dendrite growth during long solidification of Al-Cu-Li alloys: Modeling and experiment

3D characterization and modeling of low cycle fatigue damage mechanisms at high temperature in a cast aluminum alloy

Fatigue Life Assessment of a Porous Casting Nickel-Based Superalloy Based on Fracture Mechanics Methodology

Fatigue Cracking Behaviors and Influence Factors of Cast Magnesium Alloys

Modeling of microporosity evolution and fatigue life of aluminum alloy castings

On the Failure Mechanism for High Pressure Die Casting A390 Hypereutectic Alloy in Low Cycle and High Cycle Fatique

The Impact of HIP Process and Heat Treatment on the Mechanical Behaviour of an Al–Si–Mg Alloy Component

Fatigue Life Evaluation of High Pressure Hydrogen Storage Vessel

Investigation of Surface Fatigue Microcrack Growth Behavior of Cast Mg–Al Alloy

Crack Configuration Feature and Fracture Surface Difference for High Pressure Die Casting Hypereutectic Al-Si Alloys in High Cycle Fatigue

Effects of Distance and Alignment Holes on Fatigue Crack Behaviors of Cast Magnesium Alloys

Influence of Multi-Holes on Fatigue Behaviors of Cast Magnesium Alloys Based on In-Situ Scanning Electron Microscope Technology

Casting defects and fatigue strength of a die cast aluminium alloy: a comparison between standard specimens and production components

Quantitative Analysis of 3D Pore Characteristics Effect on the Ductility of HPDC Al-10Si-0.3Mg Alloy through X-Ray Tomography