Giant energy density and high efficiency achieved in silver niobate-based lead-free antiferroelectric ceramic capacitors via domain engineering

Song Li,Tengfei Hu,Hengchang Nie,Zhengqian Fu,Chenhong Xu,Fangfang Xu,Genshui Wang,Xianlin Dong

DOI: https://doi.org/10.1016/j.ensm.2020.09.021

IF: 20.4

2021-01-01

Energy Storage Materials

Abstract:<p>Dielectric materials have drawn increasing attention due to their high power density and fast charge-discharge speed. Although satisfactory energy storage performance has been achieved in lead-based ceramics, the exploration of suitable lead-free substitutions is highly desired since the rising environmental concerns caused by lead-based compounds. Herein, we demonstrate that a giant recoverable energy density of 7.01 J cm⁻³ together with high energy efficiency under 476 kV cm⁻¹, as well as impressive frequency stability (maximum variation &lt; ±3% at 1−100 Hz) and thermal stability (maximum variation &lt; ±10% over 25−120°C) under 320 kV/cm, can be obtained in Lanthanum (La)-modified AgNbO₃ ceramics. It is revealed that the long-range antiferroelectric order in AgNbO₃ is interrupted by the incorporation of La, resulting in the transformation of micron-scale antiferroelectric domains into antiferroelectric nanodomains with concurrently improved energy density and efficiency. Additionally, the introduction of La content greatly suppresses the ferrielectricity of AgNbO₃ and enhances the dielectric breakdown strength up to 494 kV cm⁻¹ versus 178 kV cm⁻¹ for the pure AgNbO₃ ceramics. These results not only reveal the high potential of La-modified AgNbO₃ ceramics for energy storage applications but also open up a feasible approach of domain engineering to develop new lead-free energy-storage dielectric materials.</p>

materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology