Oxygen Self-Doping Bi2S3@C Spheric Successfully Enhanced Long-Term Performance in Lithium-Ion Batteries

Xiaojing Zhang,Jing Xie,Yakun Tang,Zhenjiang Lu,Jindou Hu,Yang Wang,Yali Cao

DOI: https://doi.org/10.1021/acsami.4c11172

2024-10-02

Abstract:High theoretical capacity of Bi2S3 propels it toward an ideal anode material for lithium-ion batteries (LIBs); however, rapid capacity attenuation and poor long-term stability are major barriers to widespread application. In this work, an oxygen self-doping strategy was utilized to synthesize O-Bi2S3@C, significantly increasing the amount of active sites for lithium-ion storage. Meanwhile, sulfur vacancies were formed to improve the electrical conductivity and ionic transport efficiency, enhance the long-term stability, and accelerate the electrochemical kinetics of Bi2S3@C. O-BSC-S1:3 anode exhibits a reversible capacity of 673.1 mAh g-1 at 0.2 A g-1. It retains a long-term capacity of 596.3 mAh g-1 over 1100 cycles at a high density of 3 A g-1 in LIBs. Moreover, the installed O-Bi2S3@C//LiCoO2 full battery offers exceptional reversible capacity and remarkable cyclability (325.2 mAh g-1 after 200 cycles) at 0.2 A g-1. The combined strategy of oxygen self-doping and sulfur vacancy effectively enhances the reversible capacity and cycling life of Bi2S3, providing an approach for the design of high-performance transition metal sulfide anodes for LIBs.