Abstract:The ammonia synthesis activities of the anti-perovskite nitrides Co3CuN and Ni3CuN have been compared to investigate the possible metal composition-activity relationship. Post-reaction elemental analysis showed that the activity for both nitrides was due to loss of lattice nitrogen rather than a catalytic process. Co3CuN was observed to convert a higher percentage of lattice nitrogen to ammonia than Ni3CuN and was active at a lower temperature. The loss of lattice nitrogen was revealed to be topotactic and Co3Cu and Ni3Cu were formed during the reaction. Therefore, the anti-perovskite nitrides may be of interest as reagents for the formation of ammonia through chemical looping. The regeneration of the nitrides was achieved by ammonolysis of the corresponding metal alloys. However, regeneration using N2 was shown to be challenging. In order to understand the difference in reactivity between the two nitrides, DFT techniques were applied to investigate the thermodynamics of the processes involved in the evolution of lattice nitrogen to the gas phase via conversion to N2 or NH3, revealing key differences in the energetics of bulk conversion of the anti-perovskite to the alloy phase, and in loss of surface N from the stable low-index N-terminated (111) and (100) facets. Computational modelling of the density of states (DOS) at the Fermi level was performed. It was shown that the Ni and Co d states contributed to the density of states and that the Cu d states only contributed to the DOS for Co3CuN. The anti-perovskite Co3MoN has been investigated as comparisons with Co3Mo3N may give an insight into the role structure type plays in the ammonia synthesis activity. The XRD pattern and elemental analysis for the synthesised material revealed that an amorphous phase was present that contained nitrogen. In contrast to Co3CuN and Ni3CuN, the material was shown to have steady state activity at 400 °C with a rate of 92 ± 15 μmol h-1 g-1. Therefore, it appears that metal composition has an influence on the stability and activity of the anti-perovskite nitrides.

Structures and ammonia synthesis activity of hexagonal ruthenium iron nitride phases

Crystallographic and Morphological Sensitivity of N2 Activation over Ruthenium

Unique Catalytic Mechanism for Ru-Loaded Ternary Intermetallic Electrides for Ammonia Synthesis

Ruthenium Complex Hydride Catalyst as a Platform for Ammonia Synthesis: The Effect of Alkali or Alkaline Earth Elements

Ternary ruthenium complex hydrides for ammonia synthesis via the associative mechanism

Ru/CeTX (T = Ti, Sc; X = Ge, Si) intermetallic catalysts for NH3 synthesis at low temperature (300 °C): insight into formulation and related mechanisms.

Size sensitivity of supported Ru catalysts for ammonia synthesis: From nanoparticles to subnanometric clusters and atomic clusters

High-pressure study on novel structure, mechanical properties and high energy density of RuN4

Phase Engineering of a Ruthenium Nanostructure toward High-Performance Bifunctional Hydrogen Catalysis

Fe3Mo3N: Crystal Structure, High‐Temperature Behavior, and Catalytic Activity for Ammonia Decomposition

Crystal Phase Engineering of Ultrathin Alloy Nanostructures for Highly Efficient Electroreduction of Nitrate to Ammonia.

Platinum-Ruthenium Single Atom Alloy as a Bifunctional Electrocatalyst toward Methanol and Hydrogen Oxidation Reactions

Synthesis and Structural Study of Substituted Ternary Nitrides for Ammonia Production

Sub-nm Ruthenium Cluster As an Efficient and Robust Catalyst for Decomposition and Synthesis of Ammonia: Break the “size Shackles”

Sub-nanometer Ru clusters on Sm2O3 obtained from a room temperature ion adsorption method for ammonia synthesis

Manipulating the Geometric and Electronic Structures of Manganese Nitrides for Ammonia Synthesis

Atomic Scale Cooperativity of Alloy Nanostructures for Efficient Nitrate Electroreduction to Ammonia in Neutral Media

Ru and RuOx Decorated Carbon Nitride for Efficient Ammonia Photosynthesis.

Ruthenium-induced Hydrolysis Effect on Fe2O3 Nanoarrays for High-Performance Electrochemical Nitrate Reduction to Ammonia

Experimental and theoretical investigations on the anti-perovskite nitrides Co3CuN, Ni3CuN and Co3MoN for ammonia synthesis

Ruthenium/titanium Oxide Interface Promoted Electrochemical Nitrogen Reduction Reaction