Fiber/hydrogel hybrid wound dressing based on eggshell membrane containing postbiotic ingredients

Neda Nazari,Rana Imani,Leila Roozbeh Nasiraie

DOI: https://doi.org/10.1016/j.bioadv.2024.214004

2024-08-22

Abstract:Skin is the largest organ in body which has important functions. Therefore, to have a healthy skin is very essential, and wound dressings are specifically designed to promote the wound healing process. The aim of this study is to prepare and characterize a fiber-hydrogel wound dressing based on eggshell membrane (ESM) enriched with postbiotic compounds extracted from Lactobacillus plantarum NIMBB003 bacteria. For this purpose, ESM was effectively separated from eggshells through acidic treatment. Then, ultrasound was used for an optimal duration of 1.89 min at 95 % of device's power to expand the pore size of ESM from 6.89 to 10.84 μm to enhance hydrogel infiltration into ESM. The hydrogel (alginate and oxidized alginate) was then infiltrated into the ESM. ATR, SEM, and weight measurement of samples showed the proper infiltration of the hydrogel within the ESM structure. However, biostability analysis revealed that alginate hydrogel was more stable in the hybrid structure compared to oxidase alginate hydrogel. Alginate infiltration into ESM, improved the ultimate strength of the ESM to 1.89 ± 0.17 MPa and water uptake degree to 368.05 % ± 24.34 %. The water vapor transmission rate of the designed dressing was 34.14 ± 1.05 mg/cm2 after 72 h, which means the proper moist management in wound bed. Finally, addition of postbiotics at a concentration of 10 mg/ml into the hydrogel improved cell proliferation in five days. Furthermore, human dermal fibroblast cells adhered to the wound dressings properly and spread along the fibers of the ESM. In general, the developed wound dressing composed of natural biomaterials with extracellular matrix-like structure, can be used effectively to assist the wound healing process.