Mechanical and electrochemical properties of carbon nanotubule-polyaniline nanowire/polyaniline nanoparticle high-strength ultra-flexible aerogel buckypaper
Yanzhi Cai,Tingting Liu,Laifei Cheng,Siyu Guo,Shaohua Huang,Zhongyi Hu,Yuhan Wang,Haiming Yu,Dengpeng Chen
DOI: https://doi.org/10.1016/j.colsurfa.2023.132868
IF: 5.518
2023-12-06
Colloids and Surfaces A Physicochemical and Engineering Aspects
Abstract:The carbon nanotube-polyaniline nanowire/polyaniline nanoparticle (CNT-PANI nw /PANI np ) aerogel buckypaper (BP) was constructed, where PANI nanoparticles were uniformly embedded into the CNT network, and a series of downhanging PANI nanowires were grown in situ on the CNT monofilaments. The aerogel BP with 80 μm thickness had a PANI load of 3.5 mg/cm 2 and a porosity of 69%. The cross-junctions between CNT monofilaments were anchored by polyvinyl alcohol gel. It had a tensile strength of 25 MPa, with a strain of 11.4%, being folded along sharp creases or violently rubbed without damage. The specific capacitance of the aerogel BP electrode decreased from 3.070 to 2.064 F/cm 2 , as the current density increased from 2 to 8 mA/cm 2 , with a capacitance retention of 67.2%. Its specific capacitance was 1.720 and 1.560 F/cm 2 after 2000 folding in halfunfolding and 200 zigzag foldingunfolding cycles, respectively, with the capacitance retention of 84.0% and 76.2%, at 8 mA/cm 2 . Its specific capacitance was 1.832 and 1.224 F/cm 2 after 2000 and 10,000 charge-discharge cycles, respectively, with the capacitance retention of 88.8% and 59.3%, at 8 mA/cm 2 . Its residual specific capacitance after 10,000 cycles was higher than most of the reported initial value of the materials with similar compositions.
chemistry, physical