Effects of multiscale porosity of decellularized platelet-rich fibrin-loaded zinc-doped magnesium phosphate scaffolds in bone regeneration
Pritish Rath,Santanu Mandal,Pratik Das,Satyabrata Nigamananda Sahoo,Samiran Mandal,Debaki Ghosh,Samit Kumar Nandi,Mangal Roy
DOI: https://doi.org/10.1039/d3tb02981f
IF: 7.571
2024-05-06
Journal of Materials Chemistry B
Abstract:In recent years, metallic ion-doped magnesium phosphate (MgP) based degradable bioceramics have emerged as an alternative bone substitute material, owing to its excellent biocompatibility, bone-forming ability, bioactivity, and controlled degradability. Conversely, incorporating a biomolecule such as decellularized platelet-rich fibrin (d-PRF) on scaffolds has certain advantages for bone tissue regeneration, particularly in enhanced osteogenesis and angiogenesis. The present study focuses on the impact of d-PRF loaded multiscale porous zinc-doped magnesium phosphate (Zn-MgP) scaffolds on biodegradability, biocompatibility, and bone regeneration. Scaffolds were fabricated through powder-metallurgy route utilizing naphthalene as porogen (porosity 5-43%). With the inclusion of higher porogen, a higher fraction of macro-porosity (>20 μm) and pore interconnectivity were observed. X-ray diffraction (XRD) studies confirmed the formation of the farringtonite phase. The developed scaffolds exhibited a minimum ultimate compressive strength (UCS) of 8.5 MPa (for 40 Naph), which lies within the range of UCS of the cancellous bone of humans (2–12 MPa). The in vitro assessment by immersing in physiological fluid yielded higher deposition of calcium phosphate compound (CaP) in response to increased macro-porosity and interconnectivity (40 Naph). Cytocompatibility assessed by MC3T3-E1 cells showed that incorporation of d-PRF coupled with increased porosity has the highest cell attachment, proliferation, and viability. For further evaluation, developed scaffolds were implanted in in vivo rabbit femur condylar defects. Radiography, SEM, OTC labelling, and histology analysis after 2 months of implantation revealed better invasion of mature osteoblastic cells into the scaffolds with enhanced angiogenesis, superior and accelerated healing of bone defects in d-PRF-incorporated higher porosity scaffolds (40 Naph). Finally, it is hypothesized that the combination of d-PRF incorporation on multiscale porosity with increased interconnectivity facilitated better bone-forming ability, good biocompatibility, and controlled degradability within and around Zn-doped MgP scaffolds.
materials science, biomaterials