3D-Printed Polycaprolactone-Based Containing Calcium Zirconium Silicate: Bioactive Scaffold for Accelerating Bone Regeneration

Hosein Emadi,Mostafa Baghani,Maryam Masoudi Rad,Bahareh Hoomehr,Majid Baniassadi,Saeid Lotfian

DOI: https://doi.org/10.3390/polym16101389

IF: 5

2024-05-14

Polymers

Abstract:There is an essential clinical need to develop rapid process scaffolds to repair bone defects. The current research presented the development of calcium zirconium silicate/polycaprolactone for bone tissue engineering utilising melt extrusion-based 3D printing. Calcium zirconium silicate (CZS) nanoparticles were added to polycaprolactone (PCL) porous scaffolds to enhance their biological and mechanical properties, while the resulting properties were studied extensively. No significant difference was found in the melting point of the samples, while the crystallisation temperature points of the samples containing bioceramic increased from 36.1 to 40.2 °C. Thermal degradation commenced around 350 °C for all materials. According to our results, increasing the CZS content from 0 to 40 wt.% (PC40) in porous scaffolds (porosity about 55–62%) improved the compressive strength from 2.8 to 10.9 MPa. Furthermore, apatite formation ability in SBF solution increased significantly by enhancing the CZS percentage. According to MTT test results, the viability of MG63 cells improved remarkably (~29%) in PC40 compared to pure PCL. These findings suggest that a 3D-printed PCL/CZS composite scaffold can be fabricated successfully and shows great potential as an implantable material for bone tissue engineering applications.

polymer science

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to develop a bioactive scaffold capable of rapidly repairing bone defects. Specifically, the researchers used melt - extrusion - based 3D printing technology to prepare a polycaprolactone (PCL) composite containing calcium zirconium silicate (CZS), aiming to accelerate the bone regeneration process by enhancing its biocompatibility and mechanical properties. The following are the specific problems mentioned in the paper:

1. **Improving biocompatibility and mechanical properties**: Although pure PCL has good biocompatibility and a low degradation rate, its mechanical strength is low and its bioactivity is insufficient. Therefore, the researchers hope to improve these properties of PCL by adding CZS nanoparticles.

2. **Enhancing bone regeneration ability**: The researchers hope that the prepared PCL/CZS composite scaffold can exhibit better bioactivity in in - vitro and in - vivo experiments, promote the proliferation and differentiation of bone cells, and thus accelerate the regeneration of bone tissue.

3. **Optimizing the 3D printing process**: The researchers hope to prepare a porous scaffold with appropriate porosity and mechanical strength through melt - extrusion - based 3D printing technology to meet the needs of clinical applications.

4. **Evaluating thermal stability and degradation characteristics**: The researchers need to evaluate the thermal stability and degradation characteristics of the PCL/CZS composite to ensure its long - term stability in the biological environment.

5. **Verifying cell compatibility and bioactivity**: Through cell culture experiments, evaluate the influence of the PCL/CZS composite scaffold on the cell viability and bioactivity of MG63 cells, and verify its potential as an implant material for bone tissue engineering.

In summary, the main objective of this paper is to solve the deficiencies of existing bone repair materials in terms of biocompatibility, mechanical properties, and bone regeneration ability by developing and evaluating the PCL/CZS composite scaffold, and to provide a scientific basis for its application in bone tissue engineering.